用于X型焊缝打底焊接的工艺方法及其焊接辅助工装技术
Welding method for X type weld seam and welding auxiliary tooling
The process method and welding auxiliary tooling for X weld bottom welding are used in the invention. A metal cylinder is selected according to the depth of the X weld groove as a welding pad for bottom welding, and the welding cushion plate is pressed by the welding auxiliary fixture rigid positioning. The process methods mainly include the following steps: according to the depth of the X weld groove, the metal cylinder is selected as the welding pad; the metal cylinder of the welding pad is positioned and installed; the welding cushion plate is used for the positioning section welding of the X weld; the bottom welding of the X type weld; the back mechanical cleaning of the bottom welding path; the bottom welding track. Bottom welding after clearing the root.
【技术实现步骤摘要】
用于X型焊缝打底焊接的工艺方法及其焊接辅助工装
本专利技术涉及一种特别针对X型焊缝打底焊接的工艺方法及其焊接辅助工装，主要适应于轨道车辆车体制造的焊接工艺过程。
技术介绍
随着轨道车辆制造技术的快速发展，在高速列车的车体制造过程中越来越多地采用轻量化与整体性能相结合的设计技术。通常地，枕梁是列车与转向架之间牵引传动的纽带,承受着拉伸和压力交变载荷，作为重要关键部件之一，其特殊的结构及承载能力对焊缝的质量和车体安全有较高的等级要求。打底焊接在枕梁X型焊缝的焊接过程中，起着很关键的作用，对整体焊缝的质量性能有着重要影响，而外界装配条件的影响、临时焊接垫板本身的材质、临时焊接垫板定位装配后与焊缝坡口面的贴紧程度及临时焊接垫板的散热条件等都对打底焊的焊缝质量产生重大影响，使打底焊缝极易出现裂纹、气孔，熔合不良等缺陷。以往采用贴附陶瓷板或不锈钢板作为焊接垫板，打底焊道背面经清根处理后发现焊道局部区域仍然存在裂纹、气孔、熔合不良等缺陷，且清根后的剩余焊缝厚度已经近达到允许再次焊接的工艺参数极限，这样既使焊缝质量难于保证，又增加了焊接返修的难度和制造成本，降低了生产效率；另一方...
【技术保护点】
一种用于X型焊缝打底焊接的工艺方法，其特征在于：包括以下步骤，根据X型焊缝坡口深度，选定金属圆柱体作为焊接垫板；对作为焊接垫板的金属圆柱体进行定位安装；使用焊接垫板做X型焊缝的定位段焊；X型焊缝的打底焊接；打底焊道的背面机械清根；打底焊道清根后的打底焊接。
【技术特征摘要】
1.一种用于X型焊缝打底焊接的工艺方法，其特征在于：包括以下步骤，根据X型焊缝坡口深度，选定金属圆柱体作为焊接垫板；对作为焊接垫板的金属圆柱体进行定位安装；使用焊接垫板做X型焊缝的定位段焊；X型焊缝的打底焊接；打底焊道的背面机械清根；打底焊道清根后的打底焊接。2.根据权利要求1所述的用于X型焊缝打底焊接的工艺方法，其特征在于：所述作为焊接垫板的金属圆柱体，优选为与通长的不锈钢圆棒；根据X型焊缝的坡口深度选定不锈钢圆棒的直径，使其定位后高于焊缝母材表面1-2毫米。3.根据权利要求2所述的用于X型焊缝打底焊接的工艺方法，其特征在于：在不锈钢圆棒作为焊接垫板的定位安装后，与X型焊缝的错边量小于1毫米。4.根据权利要求2或3所述的用于X型焊缝打底焊接的工艺方法，其特征在于：在不锈钢圆棒作为焊接垫板的定位安装后，用于X型焊缝打底焊接的定位段焊长...