The present invention relates to a kind of antistatic conductive polymer material, which is made up of raw material consisting of the following weight parts: phenolic epoxy resin 83, 95 parts, 30 metal powder, 25 thermoplastic resin, 46 parts, 35 alkali glass fiber 25, 12 Mixed ceramics, 8 magnesium silicate 0.5, 0.7 copies of magnesium stearate, graphite 8 8 15, and other parts. Benzene two formic acid two butyl ester 4 4 6, silane coupling agent 3 5 5, hydroquinone 0.2 0.4 0.4, acetone 35 45 45. The metal powder is coated by silane coupling agent to reduce the oxidation of metal powder so as to ensure that the material has a durable and good conductivity. The insulation ceramic is mixed in the polymer material, plus graphite addition, which can effectively prevent the charge accumulation and improve the antistatic property of the material.
【技术实现步骤摘要】
一种抗静电导电高分子材料
本专利技术属于高分子材料
，具体涉及一种抗静电导电高分子材料。
技术介绍
导电粘接树脂以其日益突出的环境友好性、良好的线分辨率、较低的固化温度和简单方便的维修工艺等诸多优势逐渐受到世人的青睐，并开始广泛地应用于微电子中表面元器件、集成电路、屏蔽材料和LED灯管等各个领域的封装和粘接。导电粘接树脂按其组成可分为结构型和填充型两大类。结构型是指作为导电胶基体的高分子材料本身即具有导电性的导电胶；填充型是指通常胶粘剂作为基体，而依靠添加导电性填料使胶液具有导电作用的导电胶，目前广泛使用的均为填充型导电胶。但是许多导电粘接树脂，在实际使用过程中容易发生绝缘和色变等问题，由此引发很多安全隐患，以填充性导电粘接树脂为例，发生上述现象主要是由填充的导电粒子导电性能受到破坏，长期受到阳光照射、受热老化，以及材料本身韧性差等原因引起的，当制品上静电荷累积越来越多时，会带来很大的危害。因此有必要消除静电荷的累积效应。
技术实现思路
本专利技术的目的在于提供一种抗静电导电高分子材料，具有持久良好的导电能力，能有效防止电荷累积，提高了材料抗静电性能。本专利技术...
【技术保护点】
一种抗静电导电高分子材料，其特征在于，其是由以下重量份数的原料构成：酚醛环氧树脂83‑95份、金属粉30‑50 份、热塑性树脂25‑46 份、无碱玻璃纤维25‑35 份、混合陶瓷8‑12 份、硬脂酸镁0.5‑0.7 份、石墨8‑15份、邻苯二甲酸二丁酯4‑6 份、硅烷偶联剂3‑5份、对苯二酚0.2‑0.4 份、丙酮35‑45 份。
【技术特征摘要】
1.一种抗静电导电高分子材料，其特征在于，其是由以下重量份数的原料构成：酚醛环氧树脂83-95份、金属粉30-50份、热塑性树脂25-46份、无碱玻璃纤维25-35份、混合陶瓷8-12份、硬脂酸镁0.5-0.7份、石墨8-15份、邻苯二甲酸二丁酯4-6份、硅烷...
【专利技术属性】
技术研发人员：刘存福，
申请(专利权)人：重庆华厦新力新能源汽车有限公司，
类型：发明
国别省市：重庆,50