环保纳米陶瓷复合制剂、制备方法及包含该制剂的防锈膜技术
Environmental protection nano ceramic composite preparation, preparation method and antirust membrane containing the preparation
The invention relates to an environment-friendly nano ceramic composite preparation, preparation method and rust preventive film comprising the preparation, including environmental nano ceramic composite preparation comprises mixing raw material prepared to weight said: zirconium compounds 200, 100 rare earth metal compound 10 20 copies, 10 copies of the 5 nano metal oxides 30, silane coupling agent 50, citric acid 20 30 tartaric acid 10, 20 copies, 30 copies, 20 hydroxylamine deionized water 640 805. The antirust membrane made by the environmental protection nano ceramic composite preparation has a durable antirust, excellent bonding ability and more environmental protection.
【技术实现步骤摘要】
环保纳米陶瓷复合制剂、制备方法及包含该制剂的防锈膜
本专利技术涉及金属表面防腐处理领域，具体涉及一种环保纳米陶瓷复合制剂、制备方法及包含该制剂的防锈膜。
技术介绍
一些金属制品长期暴露在空气中，与空气中的水分等接触，容易生锈。为了缓解金属制品生锈，金属防锈工艺包括采用化学或者电化学的方法对金属表面进行处理，或者在金属表面涂覆防锈涂料，避免金属直接与空气接触。传统的化学或者电化学处理金属表面的方式包括铁系磷化处理、锌系磷化处理或者铬化处理等方式。该方式不环保、并且比较繁琐，通常采用涂覆防锈涂料的方式对金属表面做防锈处理。申请公布号为CN106590180A的中国专利公开了一种防锈试样架，该试样架表面涂覆一层防锈膜，防锈膜主要包括六偏磷酸钠、氧化钠、甲基纤维素、氯化镁、磷酸二氢钾、氢氧化铝、氧化锆、柠檬酸、羟丙基二淀粉磷酸酯、复合稀土辅料以及其他助剂，提高防锈性能和机械强度。但是，防锈膜的机械强度增大之后，其容易与基材层发生剥离，不利于金属表面的防锈处理。
技术实现思路
本专利技术的目的是提供一种环保纳米陶瓷复合制剂，其具有防锈持久、粘结能力优异、更加环保。本专利技术的上...
【技术保护点】
一种环保纳米陶瓷复合制剂，其特征在于，包括以下以重量份数表示的原料混合制得：锆系化合物100‑200份、稀土金属化合物10‑20份、纳米金属氧化物5‑10份、硅烷偶联剂30‑50份、柠檬酸20‑30份、酒石酸10‑20份、羟胺20‑30份、去离子水640‑805份。
【技术特征摘要】
1.一种环保纳米陶瓷复合制剂，其特征在于，包括以下以重量份数表示的原料混合制得：锆系化合物100-200份、稀土金属化合物10-20份、纳米金属氧化物5-10份、硅烷偶联剂30-50份、柠檬酸20-30份、酒石酸10-20份、羟胺20-30份、去离子水640-805份。2.根据权利要求1所述的环保纳米陶瓷复合制剂，其特征在于：锆系化合物为氟锆酸、氟锆酸钾或者氟化锆中的一种。3.根据权利要求1所述的环保纳米陶瓷复合制剂，其特征在于：稀土金属化合物选自硝酸铈、高氯酸铈、氧化铈、硝酸镧、高氯酸镧或者氧化镧中的一种。4.根据权利要求1所述的环保纳米陶瓷复合制剂，其特征在于：纳米金属氧化物为纳米二氧化硅或者纳米二氧化钛。5.根据权利要求4所述的环保纳米陶瓷复合制剂，其特征在于：纳米金属氧化物的粒径为30-50nm。6.根据权利要求1所述的环保纳米陶瓷复合制剂，其特征在于...
【专利技术属性】
技术研发人员：刘海山，
申请(专利权)人：北京安邦之星科技有限公司，
类型：发明
国别省市：北京,11