本发明专利技术公开了一种纺织骨架材料，主要包括由主体纤维和粘合用低熔点化纤经加热模压制成的薄板状成型骨架基材，与所述基材用粘合剂复合的纺织物面料或塑料片面料，面料与面料结合处用高频焊接装饰条装饰，所述主体纤维采用服装边角料、化纤废丝、纺织下脚料制取的再生纤维，粘合用低熔点化纤为聚丙烯纤维。其优点是主体纤维粘合时不采用有毒的酚醛树脂作粘合剂，不污染环境，同时能充分利用纺织下脚料，降低生产成本。

A textile skeleton material

The invention discloses a textile reinforcing material, which mainly comprises main fibers and adhesive with low melting point fiber sheet forming frame are heated and pressed into the substrate, and the substrate with an adhesive composite textile fabric or plastic fabric, fabric and fabric with high frequency welding decorative decoration, the body fiber by using recycled fiber leftover materials of clothing, silk, chemical fiber textile waste production, adhesive with low melting point fiber for polypropylene fiber. The advantage is that when the main fiber is bonded, no toxic phenolic resin is used as an adhesive, which does not pollute the environment, and at the same time, can make full use of textile waste and reduce the production cost.

【技术实现步骤摘要】
一种纺织骨架结构材料
本专利技术属于纺织领域，具体涉及一种纺织骨架结构材料。
技术介绍
现有技术采用纤维加酚醛树脂生产内饰的生产技术，即用酚醛树脂作为粘合剂对用非织造方法生产的纤维网进行化学粘合，直接或经过模压制成低或中、高密度汽车内装饰材料。酚醛树脂粘合剂具有粘结度较高、耐热、耐燃、耐油、耐大多数化学溶剂、耐霉菌作用、尺寸稳定、高温下有较高的刚性保持率和耐蠕变性、价格低廉等优良性能。但酚醛树脂在生产、使用过程中会挥发出游离酚及游离甲醛，对环境产生污染，影响人体健康，合酚醛树脂的制品成为垃圾降解后会使地面水污染，将其焚烧又需采取专门安全措施，因此取代酚醛的开发研究十分必要。
技术实现思路
本专利技术目的是提供一种取代酚醛树脂粘合剂的的纺织骨架材料，解决了现有技术中的缺陷。本专利技术解决技术问题采用如下技术方案：一种纺织骨架结构材料，其特征在于：包括由主体纺织纤维和粘合用低熔点化学纤维组成，经混和、梳理、成网、加固后制得的毡片，并将所述毡片加热、模压制成的低或中、高密度薄片状骨架基材(1)，还包括与上述基材(1)用粘合剂复合的面料，所述面料可以是纺织装饰面料(3)或PVC面料(2)，或同时本文档来自技高网...

【技术保护点】
一种纺织骨架结构材料，其特征在于：包括由主体纺织纤维和粘合用低熔点化学纤维组成，经混和、梳理、成网、加固后制得的毡片，并将所述毡片加热、模压制成的低或中、高密度薄片状骨架基材(1)，还包括与上述基材(1)用粘合剂复合的面料，所述面料可以是纺织装饰面料(3)或PVC面料(2)，或同时为纺织装饰面料(3)和PVC面料(2)。

【技术特征摘要】
1.一种纺织骨架结构材料，其特征在于：包括由主体纺织纤维和粘合用低熔点化学纤维组成，经混和、梳理、成网、加固后制得的毡片，并将所述毡片加热、模压制成的低或中、高密度薄片状骨架基材(1)，还包括与上述基材(1)用粘合剂复合的面料，所述面料可以是纺织装饰面料(3)或PVC面料...

【专利技术属性】
技术研发人员：徐彪，缪正伟，
申请(专利权)人：江阴市海特网络科技有限公司，
类型：发明
国别省市：江苏,32