The invention discloses a graphene oxide (GO) porous chitosan membrane Pickering emulsion preparation method comprises the following steps: stable, ultrasonic treatment in deionized water adding amount of GO prepared GO suspension liquid; chitosan solution was added to dissolve the GO suspension, and adding benzoic acid esters as the oil phase, ultrasonic treatment; after the sample is placed in water pouring under crosslinked membrane; membrane will not pay even in impregnation solution containing a crosslinking agent in a period of time to the crosslinking, ran with ethanol and deionized water for cleaning, the membrane drying, chitosan membrane has a porous structure is obtained. The preparation of Pickering porous chitosan membrane emulsion preparation process is simple, green, low requirement on equipment, water solution with high stability, uniform porous structure, easy to scale, has a broad application prospect in the field of food preservation, wastewater treatment, food preservation, catalysis, heavy metal ion detection.
【技术实现步骤摘要】
一种氧化石墨烯(GO)稳定的Pickering乳液制备多孔壳聚糖膜的制备方法
本专利技术涉及多孔壳聚糖膜的制备领域，特别涉及一种氧化石墨烯(GO)稳定的Pickering乳液制备多孔壳聚糖膜的制备方法。
技术介绍
聚合物膜在水分离和过滤工业中起着至关重要的作用。然而，其制备过程用到大量的有毒有机溶剂，且有机溶剂的后处理十分昂贵。由于生物基聚合物的可再生性，生物基聚合物可以用来替代石油基聚合物。但从生物基聚合物制备多孔膜仍有许多缺点需要克服：(1)与石油基聚合物相比，大多数生物基聚合物是水溶性的；因此，为了在含水条件下的应用，使其能够在水中保持结构稳定十分必要。(2)制备过程中的温度变化会引起其构象的强烈改变(例如物理凝胶化，淀粉糊化和老化)进而限制了其使用范围。由于这些特定的性质，利用普通的方法直接使生物基聚合物具有多孔结构不会使其具有很好的综合性能。甲壳素(chitin)是地球上除了纤维素外第二大生物质有机资源，其年生物合成量大约为100亿吨，来源十分丰富。壳聚糖(chitosan，CTS)是甲壳素在碱性条件下水解并脱去部分乙酰基后生成的衍生物，可以溶解...
【技术保护点】
一种氧化石墨烯(GO)稳定的Pickering乳液制备多孔壳聚糖膜的制备方法，其特征在于包括下面步骤：步骤一：在去离子水中加入适量的GO，制得浓度为0.1‑8g.L
【技术特征摘要】
1.一种氧化石墨烯(GO)稳定的Pickering乳液制备多孔壳聚糖膜的制备方法，其特征在于包括下面步骤：步骤一：在去离子水中加入适量的GO，制得浓度为0.1-8g.L-1的GO悬浮分散液，乳化机分散处理10-60min；将5-40％W/V的壳聚糖溶液在25-50℃下加入到GO悬浮液中溶解，加入苯甲酸酯类作为油相，油水体积比(O/W)为0.2-0.8，通过乳化机分散处理5-20min，放置在35-65℃的水浴中0.5～2h后浇注成膜，然后在35-65℃下放置2-4天...
【专利技术属性】
技术研发人员：罗静，陈亚鑫，樊效宗，吴凯云，朱叶，刘晓亚，
申请(专利权)人：江南大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。