一种耐波峰焊PVC绝缘芯线料制造技术

本发明专利技术公开了一种耐波峰焊PVC绝缘芯线料，包括按重量份数计的以下组份：PVC粉358～438份；高岭土36～44份；活性碳酸钙323～395份；增塑剂154～188份；稳定剂21.6～26.4份；硬脂酸钙2.7‑3.3份；PE蜡2.7～3.3份；色粉1.44～1.76份。本发明专利技术的耐波峰焊PVC绝缘芯线料成本低，线料过265度波峰焊后胶皮上缩<0.5mm；且本发明专利技术的配方环保无毒，可用于制做3岁以下的玩具，符合国际ROHS、2005/84/EC、REACH、PAHs、EN71‑3等玩具法规环保要求。

A kind of PVC insulated core wire for wave soldering

The invention discloses a resistance to soldering of PVC insulating core wire material, comprising the following components by weight: PVC powder 358~438 parts; kaolin 36~44; active calcium carbonate 323~395; plasticizer stabilizer 154~188; 21.6 ~ 26.4; 2.7 calcium stearate 3.3; PE wax 2.7 ~ 3.3 a toner 1.44 ~ 1.76. The invention of the resistance to soldering of PVC cable material cost is low, the line is expected over 265 degrees after soldering on the rubber shrink < 0.5mm; and the formula of the invention are non-toxic, can be used for making toys under the age of 3, in line with the international ROHS, 2005/84/EC, REACH, PAHs, EN71 3 toys environmental protection regulations request.

【技术实现步骤摘要】
一种耐波峰焊PVC绝缘芯线料
本专利技术涉及电线电缆胶料
，尤其涉及一种耐波峰焊PVC绝缘芯线料。
技术介绍
随着机械化的普及，行业上为降低人工成本，PCB板的焊接慢慢由人手焊接转向波峰焊过渡，旧的手焊配方胶料电线，在过波峰焊时，因升温久，受热时间长，焊后线口胶皮上缩较为严重，铜丝裸露长，易与其它元件接触短路等问题；随着焊接环境的改变，需要耐波峰焊的耐温胶料，降低缩胶，从而实现电线在过波峰焊后不缩胶不露铜，有效的保护元件与电线之间的绝缘问题。
技术实现思路
本专利技术的目的在于提供一种耐波峰焊PVC绝缘芯线料。为解决以上技术问题，本专利技术采用的技术方案是：一种耐波峰焊PVC绝缘芯线料，包括按重量份数计的以下组份：优选的，包括按重量份数计的以下组份：优选的，所述PVC粉为PVC粉S-60，K值59.2-60.6，膠化性佳且透明性佳。本专利技术配方选用的高岭土具有很高的耐火度，提高胶料机械强度，耐热性能。优选的，所述活性碳酸钙为纳米级活性碳酸钙，纳米级活性碳酸钙能够使PVC钢性增大，减少胶料收缩率，提高耐热性能，具有阻燃作用，且能够减少原材料用量，降低成本。优选的，所述增塑剂为DIN本文档来自技高网...

【技术保护点】
一种耐波峰焊PVC绝缘芯线料，其特征在于，包括按重量份数计的以下组份：

【技术特征摘要】
1.一种耐波峰焊PVC绝缘芯线料，其特征在于，包括按重量份数计的以下组份：2.根据权利要求1所述的一种耐波峰焊PVC绝缘芯线料，其特征在于，包括按重量份数计的以下组份：3.根据权利要求1或2所述的一种耐波峰焊PVC绝缘芯线料，其特征在于：所述PV...