Manufacturing method of aluminum joint

A method of manufacturing an aluminum joint that can ensure the diameter of the beam spot to ensure the bonding strength and to reduce the crack in the molten solidification part is provided. Aluminum assembly manufacturing method comprises the following steps: overlapping electrical conductivity than the first aluminum components in the first aluminum component (31) of second high aluminum components (33), and the first aluminum member (31) formed the lap joint process; aluminum components from second side irradiation energy beam is formed through melting and solidification of the lap the joint (35) of the energy beam welding process.

【技术实现步骤摘要】
铝接合体的制造方法
本专利技术涉及铝接合体的制造方法。
技术介绍
近年来，在汽车中，为了提高燃油效率而必须使构件轻量化。铝或铝合金因为轻量、且比强度(单位重量下的强度)大，轻量化成本也低，所以适于量产。那么，激光焊接等的能束焊接，既能够减少线能量，又能够形成深熔深的接合部。此外近年来，一边由反射镜扫描激光束一边进行焊接的所谓遥控焊接正在普及。在这样的遥控焊接中，可以对激光束进行圆周状、螺旋状(涡旋状)、平行线状、Z字状等各种形态下的扫描(例如参照专利文献1)。在铝或铝合金这样的热膨胀系数大的材料中，因为熔融部急速凝固，所以容易发生裂纹。特别是在点焊(光束点焊)中，熔融部沿周向被拉伸，因此更容易发生裂纹。因此，为了缓和熔融部的凝固速度，已知一种方法，其通过在形成点状的熔融凝固部后，包围该熔融凝固部的外周而扫描激光束，以缓和熔融部的凝固速度，从而抑制裂纹(例如参照专利文献2)。另外，还已知有一种方法，其通过一边缩小束斑直径，一边依次减小束斑对多个照射区域的热量而进行光束照射并焊接，由此抑制熔融凝固部的大小的偏差，抑制裂纹(例如参照专利文献3)。现有技术文献专利文献专利文献1：日本特开20本文档来自技高网...

【技术保护点】
一种铝接合体的制造方法，其具有如下工序：在第一铝构件上重叠导电率比所述第一铝构件高的第二铝构件，使其和所述第一铝构件形成搭接接头的工序；从所述第二铝构件侧照射高能束，形成贯通所述搭接接头的熔融凝固部的能束焊接工序。

【技术特征摘要】
2016.09.14 JP 2016-1800011.一种铝接合体的制造方法，其具有如下工序：在第一铝构件上重叠导电率比所述第一铝构件高的第二铝构件，使其和所述第一铝构件形成搭接接头的工序；从所述第二铝构件侧照射高能束，形成贯通所述搭接接头的熔融凝固部的能束焊接工序。2.根据权利要求1所述的铝接合体...

【专利技术属性】
技术研发人员：青木拓朗，松本刚，北村智之，
申请(专利权)人：株式会社神户制钢所，
类型：发明
国别省市：日本,JP