The invention relates to an injection molding with environment-friendly heat-resistant PVC particles, the heat-resistant PVC particles prepared by extrusion mechanism, the heat-resistant PVC particles by the following components in part by weight: S resin 60 100 copies, two copies, 2~5 dioctyl terephthalate liquid stabilizer 2~5, calcium carbonate, 6~10 0.5~2 ACR, a lubricant acrylate copolymer 10~20, chlorinated polyethylene 10~15, alpha two MS dimer 8~15. The injection molding environment-friendly heat resistant rigid PVC colloidal particle has high impact strength, high hardness and environmental protection requirements, and meanwhile, it satisfies the injection processing temperature wide, the product fluidity is good, and the surface finish is high.
【技术实现步骤摘要】
注塑用环保型耐热硬质PVC胶粒
本专利技术涉及一种排水管件接口、硬质塑料垫片等注塑行业用材料,尤其涉及一种注塑用环保型耐热硬质PVC胶粒。
技术介绍
硬质聚氯乙烯塑料是不加或少加增塑剂的,这种以聚氯乙烯树脂及稳定剂为主体的塑料制品,就必然造成硬质聚氯乙烯塑料流动性差的特点。因此,为了保证塑料有一定程度的流动性,必须提高加工温度。但是加工温度的提高是有一定限度的,如果超过分解温度就会破坏正常操作。因此在配方设计时必须考虑硬质聚氯乙烯塑料的加工温度与分解温度比较接近的特点,以尽量选用合理的配方来弥补这些缺陷。同时硬质聚氯乙烯塑料用于注塑成型方面,必项考虑下列四个特点:(1)热稳定性好,在成型温度及一定的停留时间内,不致引起分解;(2)流动性能好,在一定的温度下,能顺利地充满复杂的模腔;(3)收缩性小,脱模方便,如为螺纹连接的产品,要考虑到装配方便;(4)耐腐蚀性好及耐热性高,以扩大使用范围。
技术实现思路
本专利技术的目的是提供一种注塑用环保型耐热硬质PVC胶粒,该注塑用环保型耐热硬质PVC胶粒抗冲强度高、硬度高、环保要求,同时满足注塑加工温度宽,产品流动性好,表面光洁度高指标。为达到上述目的,本专利技术采用的技术方案是:一种注塑用环保型耐热硬质PVC胶粒,所述耐热硬质PVC胶粒由挤塑机制备而成,此耐热硬质PVC胶粒由以下重量份的组分组成:S-60树脂100份,对苯二甲酸二辛脂2~5份,液体稳定剂2~5份,碳酸钙6~10份,润滑剂0.5~2份,ACR丙烯酸酯类共聚物10~20份,氯化聚乙烯10~15份,α-MS二聚体8~15份。上述技术方案中进一步改进的技术方案如 ...
【技术保护点】
一种注塑用环保型耐热硬质PVC胶粒,其特征在于:所述耐热硬质PVC胶粒由挤塑机制备而成,此耐热硬质PVC胶粒由以下重量份的组分组成:S‑60树脂 100份,对苯二甲酸二辛脂 2~5份,液体稳定剂 2~5份,碳酸钙 6~10份,润滑剂 0.5~2份,ACR丙烯酸酯类共聚物 10~20份,氯化聚乙烯 10~15份,α‑MS二聚体 8~15份。
【技术特征摘要】
1.一种注塑用环保型耐热硬质PVC胶粒,其特征在于:所述耐热硬质PVC胶粒由挤塑机制备而成,此耐热硬质PVC胶粒由以下重量份的组分组成:S-60树脂100份,对苯二甲酸二辛脂2~5份,液体稳定剂2~5份,碳酸钙6~10份,润滑剂0.5~2份,ACR丙烯酸酯类共聚物10~20份,氯化聚乙烯10~15份,α-MS二聚体8~15份。2.根据权利要求1...