The invention relates to a low temperature resistant weatherability of PVC pipe and its production method, which is characterized in that comprises the following raw materials in parts by weight: among them, 100 copies, 80 PVC resin modified kaolin 10 20 copies, 5 copies, 2 stabilizer modifier 1 3 copies, 2 copies of PE 0.5 wax plasticizer 0.5 1 copies, 0.5 copies of the 0.2 composite antioxidants. The modified kaolin is used as a filling agent. The raw material is simple and easy to get, and the cost is low. With the addition of admixtures, the PVC pipe has great resistance to low temperature, and has good weatherability, anti-aging ability and impact resistance.
【技术实现步骤摘要】
耐低温耐候性PVC管及其生产方法
本专利技术属于PVC管的加工领域，特别是涉及一种耐低温耐候性PVC管及其生产方法。
技术介绍
塑料管材是高科技复合而成的化学建材，而化学建材是继钢材、木材、水泥之后，当代新兴的第四大类新型建筑材料。化学建材在我国取得了长足进步迅猛发展，尤其是新型环保塑料管材的广泛使用，掀起了一声替代传统建材的革命。塑料管材因具有水流损失小、节能、节材、保护生态、竣工便捷等优点，广泛应用于建筑给排水、城镇给排水以及燃气管等领域，成为新世纪城建管网的主力军。塑料和传统材料不同，技术进步的的步伐更快，不断的出现的新技术、新材料、新工艺使塑料管相对传统材料的优势越来越突出。塑料管材与传统的金属管相比，具有重量轻，一般仅为金属管的1/6-1/10，有较好的耐腐蚀性，抗冲击和抗拉强度，塑料管内表面比铸铁管光滑的多、摩擦系数小、流体阻力小、可降低输水能耗5％以上，综合节能好，制造能耗右降低75％，运输方便，安装简单，使用寿命长达30-50年。塑料管材在世界各国发展很快，发达国家在给水领域和燃气领域应用已占绝对的优势塑料管材不但大量用来代替传统的钢管、铸铁管等，...
【技术保护点】
一种耐低温耐候性PVC管，其特征在于，包括以下重量份数的原料：其中，聚氯乙烯树脂80‑100份、改性高岭土10‑20份、稳定剂2‑5份、改性剂1‑3份、PE蜡0.5‑2份、增塑剂0.5‑1份、复合抗氧化剂0.2‑0.5份。
【技术特征摘要】
1.一种耐低温耐候性PVC管，其特征在于，包括以下重量份数的原料：其中，聚氯乙烯树脂80-100份、改性高岭土10-20份、稳定剂2-5份、改性剂1-3份、PE蜡0.5-2份、增塑剂0.5-1份、复合抗氧化剂0.2-0.5份。2.根据权利要求1所述的耐低温耐候性PVC管，其特征在于：所述改性高岭土的制备方法为将研磨后的高岭土加入搅拌器中，加热至120℃，搅拌10min，然后缓慢加入占高岭土总量1％的偶联剂，偶联剂加完后保持温度在120℃，继续搅拌10-20min，即得改性高岭土。3.根据权利要求1所述的耐低温耐候性PVC管，其特征在于：所述稳定剂的成分包括环氧大豆油、有机锡、硬脂酸钙和钡锌稳定剂；环氧大豆油、有机锡、硬脂酸钙、钡锌稳定剂的质量比为2-3:2:3-4:1。4.根据权利要求1所述的耐低温耐候性PVC管，其特征在于：所述改性剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物。5.根据权利要求1所述的耐低温耐候性PVC...
【专利技术属性】
技术研发人员：梁洪昌，
申请(专利权)人：广西金滩管业科技有限公司，
类型：发明
国别省市：广西,45