一种舱段及其加工方法技术

本发明专利技术提供了一种舱段及其加工方法，涉及机械加工技术领域，通过该加工方法制作的舱段具有低成本且质量高的特点。一种舱段的加工方法，所述方法包括：对待加工圆锭进行挤压或者锻造以形成毛坯管，所述待加工圆锭的材料为轻质结构材料；对所述毛坯管进行至少一次预处理；所述预处理包括：第一热处理、拉拔和第二热处理；对经过至少一次预处理后的所述毛坯管进行机加工，以形成舱段。本发明专利技术适用于舱段的制作。

A cabin and its processing method

The present invention provides a structure and processing method thereof, relates to the technical field of mechanical processing, made by the processing method of the cabin has the characteristics of low cost and high quality. A method for processing section, the method includes: processing of extrusion or treat round ingot forging to form blank pipe, the processing of round billet material for lightweight structural materials; at least one pretreatment on the blank tube; the pretreatment includes: first, second heat drawing and heat treatment after the treatment; the blank at least once after pretreatment of the tube is machined to form a cabin. The invention is applicable to the production of cabin.

【技术实现步骤摘要】
一种舱段及其加工方法
本专利技术涉及机械加工
，尤其涉及一种舱段及其加工方法。
技术介绍
舱段作为飞船、导弹的重要组成部分，在军事领域有着广泛应用。传统技术中，采用“板材卷曲→焊接→机加工”的加工工艺制作舱段。但是，该加工工艺中包括的焊接工艺操作复杂、成本过高；传统舱段的加工工艺已经不能满足目前军事装备对于低成本的要求。如何在保证舱段质量的前提下，降低舱段的生产成本已经成了亟待解决的问题。
技术实现思路
本专利技术的实施例提供一种舱段及其加工方法，通过该加工方法制作的舱段具有低成本且质量高的特点。为达到上述目的，本专利技术的实施例采用如下技术方案：一方面，提供了一种舱段的加工方法，所述方法包括：对待加工圆锭进行挤压或者锻造以形成毛坯管，所述待加工圆锭的材料为轻质结构材料；对所述毛坯管进行至少一次预处理；所述预处理包括：第一热处理、拉拔和第二热处理；对经过至少一次预处理后的所述毛坯管进行机加工，以形成舱段。可选的，所述第一热处理包括：固溶处理和时效处理，所述第二热处理包括：退火。可选的，在所述第一热处理之后、且在所述拉拔之前，所述预处理还包括：酸洗处理。可选的，在对所述毛坯管进行至少本文档来自技高网...

【技术保护点】
一种舱段的加工方法，其特征在于，所述方法包括：对待加工圆锭进行挤压或者锻造以形成毛坯管，所述待加工圆锭的材料为轻质结构材料；对所述毛坯管进行至少一次预处理；所述预处理包括：第一热处理、拉拔和第二热处理；对经过至少一次预处理后的所述毛坯管进行机加工，以形成舱段。

【技术特征摘要】
1.一种舱段的加工方法，其特征在于，所述方法包括：对待加工圆锭进行挤压或者锻造以形成毛坯管，所述待加工圆锭的材料为轻质结构材料；对所述毛坯管进行至少一次预处理；所述预处理包括：第一热处理、拉拔和第二热处理；对经过至少一次预处理后的所述毛坯管进行机加工，以形成舱段。2.根据权利要求1所述的加工方法，其特征在于，所述第一热处理包括：固溶处理和时效处理，所述第二热处理包括：退火。3.根据权利要求1所述的加工方法，其特征在于，在所述第一热处理之后、且在所述拉拔之前，所述预处理还包括：酸洗处理。4.根据权利要求1所述的加...

【专利技术属性】
技术研发人员：刘瑶，宋方，
申请(专利权)人：西安方元明科技股份有限公司，
类型：发明
国别省市：陕西,61