The present invention relates to the field of new materials, in particular to a special laser 3D printing high hardness alloy of nickel based alloy powder, which comprises the following weight percentage of the raw material: 0.9 - 1.3% carbon (C), 2 - 2.5% of tungsten (W), 20 - 25% of the chromium (Cr), 1.2 - 1.6% of titanium (Ti 2 - 2.5%), molybdenum (Mo), 1 - 1.5% V (V), 0.15 - 0.7% (Nb), niobium nickel (Ni), margin and its weight is 100%; the purpose of the invention is to provide a special laser 3D printing high hardness alloy of nickel based alloy powder to adjust the powder, add carbon content is higher, can not only ensure that the laser print 3D parts with no crack, but also can improve the hardness and wear resistance of parts, greatly improving the quality of laser printed 3D parts.
【技术实现步骤摘要】
一种激光3D打印高硬度镍基合金专用合金粉末
本专利技术涉及新材料领域，尤其涉及一种激光3D打印高硬度镍基合金专用合金粉末。
技术介绍
激光3D打印技术是一种先进制造技术，该技术通过高功率激光熔化原料粉末或丝材，在沉积基板的配合运动下，逐点逐层堆积材料，通过不断生长制备出零件；国内外金属3D打印机采用的金属粉末一般有：不锈钢、钛合金、铝合金、镍基合金和钴铬合金等；激光3D打印镍基合金零件因具有良好的耐腐蚀﹑耐氧化和价格适中等优点具有广阔用途；目前用于激光3D打印的镍基合金材料主要有：IN718、IN625、80NiCr和C276等；采用现有的合金粉末作为原料用于激光3D打印镍基合金存在一定的缺陷：（1）合金零件硬度不高，基本在45HRC以下，导致零件耐磨性不高；（2）镍基合金材料一般只能在完全充氩环境条件下使用，不能在空气环境或局部充氩环境条件下使用，否则就会有较多氧化物夹杂，影响零件性能（如塑性﹑抗拉强度和疲劳性能等），这就极大限制了3D打印零件的尺寸。
技术实现思路
本专利技术的目的是提供一种激光3D打印高硬度镍基合金专用合金粉末，对粉末的成分进行调整，添加较高含量...
【技术保护点】
一种激光3D打印高硬度镍基合金专用合金粉末，其特征在于，包括下述重量百分数的原料：0.9—1.3%的碳（C），2.0—2.5%的钨（W），20.0—25.0%的铬（Cr），1.2—1.6%的钛（Ti），2.0—2.5%的钼（Mo），1.0—1.5%的钒（V），0.15—0.7%的铌（Nb），余量为镍（Ni），其重量之和为100%。
【技术特征摘要】
1.一种激光3D打印高硬度镍基合金专用合金粉末，其特征在于，包括下述重量百分数的原料：0.9—1.3%的碳（C），2.0—2.5%的钨（W），20.0—25.0%的铬（Cr），1.2—1.6%的钛（Ti），2.0—2.5%的钼（Mo），1.0—1.5%的钒（V），0.15—0.7%的铌（Nb），余量为镍（Ni），其重量之和为100%。2.根据权利要求1所述的一种激光3D打印高硬度镍基合金专用合金粉末，其特征在于，包括下述重量百分数的原料：1.1%的碳（C），2...
【专利技术属性】
技术研发人员：李胜，谢春晓，韩立发，黄楚刁，邹建军，蔡志祥，
申请(专利权)人：东莞理工学院，深圳光韵达光电科技股份有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。