The invention provides a mold heat treatment process, which comprises the following steps: A, preparation of heat treatment of die mold, no allowance for heat treatment after once processing; B, annealing, annealing temperature of 400 DEG C 650, 1 2 hours; C, quenching, quenching temperature 860 C 980 C 2, 4 hours, 4 minutes and 3 selection of oil cooling; D, tempering, tempering temperature of 150 DEG 250 DEG C for 5 hours, 6 hours; E, aging treatment, heating to 100 DEG C 150 DEG C for 10 to 15 hours. F, air cooling, the aging of the treatment of the kernel to cool to room temperature. The invention provides a kernel heat treatment process. The aging treatment after tempering can effectively remove the residual stress and increase the strength and hardness.
【技术实现步骤摘要】
一种模仁热处理工艺
本专利技术涉及一种热处理工艺，特别涉及一种模仁热处理工艺。
技术介绍
热处理是指材料在固态下，通过加热、保温和冷却的手段，以获得预期组织和性能的一种金属热加工工艺。现阶段的模仁需要经过热处理提高其硬度与各项的性能，现有技术中的模仁热处理不能够完全去除内应力。
技术实现思路
【1】要解决的技术问题本专利技术要解决的技术问题是提供一种能够完全去除残留应力的模仁热处理工艺。【2】解决问题的技术方案一种模仁热处理工艺，其特征在于，包括以下步骤：a、制备热处理的模仁,模仁留有余量便于热处理后进一度加工；b、退火处理，退火温度为400℃-650℃，保持1-2小时；c、淬火处理，淬火温度为860℃-980℃，保持2-4小时，选用油冷却3-4分钟；d、回火处理，低温回火温度为150℃-250℃，持续5小时-6小时；e、时效处理，加热至100℃-150℃持续10-15小时。f、风冷，将时效处理后的模仁冷却至室温。【3】有益效果本专利技术提供模仁热处理工艺，回火后进行时效处理能够有效地去除残留的应力，增加了强度与硬度。具体实施方式下面详细介绍本专利技术实施例。一种模仁...
【技术保护点】
一种模仁热处理工艺，其特征在于，包括以下步骤：a、制备热处理的模仁,模仁留有余量便于热处理后进一度加工；b、退火处理，退火温度为400℃‑650℃，保持1‑2小时；c、淬火处理，淬火温度为860℃‑980℃，保持2‑4小时，选用油冷却3‑4分钟；d、回火处理，低温回火温度为150℃‑250℃，持续5小时‑6小时；e、时效处理，加热至100℃‑150℃持续10‑15小时。f、风冷，将时效处理后的模仁冷却至室温。
【技术特征摘要】
1.一种模仁热处理工艺，其特征在于，包括以下步骤：a、制备热处理的模仁,模仁留有余量便于热处理后进一度加工；b、退火处理，退火温度为400℃-650℃，保持1-2小时；c、淬火处理，淬火温度为860℃-980...