The invention discloses a method for preparing high strength and high plasticity stainless steel furnace bracket, which comprises the following steps: the mold insulation ECAP austenitic stainless steel sample in the pre heating period, after repeated extrusion, the specimen is removed in a heat treatment furnace, annealing, cooling to room temperature to obtain high strength high plastic stainless steel, the invention uses ECAP process to fabricate single nanocrystalline structure of stainless steel, then carries on the annealing treatment, by controlling the process parameters, to achieve a single nanocrystal structure to change dual scale structure, improve the strength, use of ultrafine grained coarse grained plastic part part of the recovery, to obtain a high strength, a new type of stainless steel high performance plastic excellent.
【技术实现步骤摘要】
一种用于炉支架的高强度高塑性不锈钢的制备方法
本专利技术属于铸造
，具体涉及一种用于炉支架的高强度高塑性不锈钢的制备方法。
技术介绍
不锈钢材料以其优异的耐腐蚀性能和一定的力学性能成为工业和军事发展不可或缺的重要工程材料，应用范围遍及石油、化工、纺织、厨具等各个领域，随着现代化工、家电、医疗器械等事业的进一步发展，对不锈钢的性能也提出了更高的使用要求，通常奥氏体不锈钢存在强度和硬度较低的不足，使得由奥氏体不锈钢制成的产品易发生屈服变形引起失效或者磨损，从而降低产品的使用寿命，因此需开发一些特殊工艺来提高奥氏体不锈钢的强度和硬度，从而达到改善材料性能、提高产品质量的目的。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种用于炉支架的高强度高塑性不锈钢的制备方法，该方法先制备得到超细晶/纳米晶化奥氏体不锈钢，通过对其进行热处理，获得粗晶+超细晶/纳米晶的双尺度结构，利用粗晶结构来恢复不锈钢的良好塑性，同时利用超细晶/纳米晶结构保持其高强度，从而达到获取高强度、高塑性不锈钢的目的。本专利技术提供的一种用于炉支架的高强度高塑性不锈钢的...
【技术保护点】
一种用于炉支架的高强度高塑性不锈钢的制备方法，其特征在于：包括以下步骤：1）把奥氏体不锈钢试样放入预加热的ECAP模具内，预加热的ECAP模具温度为600℃～700℃，保温；2）挤压5～10道次，挤压的速度为120～280mm/min，挤压路径为Bc；3）多次挤压后，取出试样放入热处理炉内，进行退火处理，退火处理的工艺为在800～1000℃下处理30～55min；4）空冷至室温，得到高强度高塑性不锈钢。
【技术特征摘要】
1.一种用于炉支架的高强度高塑性不锈钢的制备方法，其特征在于：包括以下步骤：1）把奥氏体不锈钢试样放入预加热的ECAP模具内，预加热的ECAP模具温度为600℃～700℃，保温；2）挤压5～10道次，挤压...
【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37