The invention discloses a kind of epoxy resin for high weatherability composite material. According to the following methods of preparation and the polyvinyl alcohol resin, ethyl methacrylate at the temperature of 120~140 DEG C under stirring for 30 ~ 40min, filtration; filtrate obtained by adding sorbic acid, at 20~30 DEG C temperature mixing; adding polyols and catalysts, at 20~30 DEG C temperature mixing 5 10min high weatherable epoxy resin; the raw material components in parts by weight: 95 polyvinyl alcohol resin are as follows: 105; 80: 50 ethyl methacrylate; sorbic acid: 200 230; 1 polyol: 1.5; catalyst: 1 1.5. The epoxy resin formulation of the high weatherability composite material of the invention has the advantages of simple formulation, low cost and good manufacturability. The fiber reinforced epoxy composite material has good mechanical properties, excellent color resistance and excellent weather resistance.
【技术实现步骤摘要】
一种高耐候性复合材料用环氧树脂
本专利技术属于高分子材料领域，具体涉及一种高耐候性复合材料用环氧树脂。
技术介绍
纤维增强环氧树脂复合材料制品在户外使用时，会受到光、热、氧、潮湿、水分等气候因素作用，引起微观结构的破坏，失去原有的物理机械性能，同时还会使材料老化变色，最终丧失使用价值。气候因素会影响复合材料的基体、内部纤维、复合材料界面这三个方面，其中基体的耐候性对复合材料耐候性起主要作用。复合材料常用的双酚A型环氧树脂由于分子结构中有苯环、双键的存在，在紫外线照射下、湿热环境下树脂基体中的苯环、双键会被破坏，从而使材料发生老化。在纤维增强环氧树脂复合材料制品的制备过程中，通过研制或选用耐候性的原材料，或者在环氧树脂中加入抗老化助剂的方法来提高纤维增强复合材料的耐候性。
技术实现思路
本专利技术的目的是提供一种配方及制备方法简单，力学性能良好，具有出色的抗色变性能和优秀耐候性的高耐候性复合材料用环氧树脂。一种高耐候性复合材料用环氧树脂，其特征在于按以下方法制备而来：将聚乙烯醇树脂、甲基丙烯酸乙酯于120～140℃温度下搅拌反应30～40min，过滤；所得滤液中加入己二...
【技术保护点】
一种高耐候性复合材料用环氧树脂，其特征在于按以下方法制备而来：将聚乙烯醇树脂、甲基丙烯酸乙酯于120～140℃温度下搅拌反应30～40min，过滤；所得滤液中加入己二烯酸，于20～30℃温度下搅拌混合均匀；加入多元醇和催化剂，于20～30℃温度下搅拌混合5‑10min，得到高耐候性环氧树脂；所用原料按质量份数计如下：聚乙烯醇树脂：95‑105份；甲基丙烯酸乙酯：50‑80份；己二烯酸：200‑230份；多元醇：1‑1.5份；催化剂：1‑1.5份。
【技术特征摘要】
1.一种高耐候性复合材料用环氧树脂，其特征在于按以下方法制备而来：将聚乙烯醇树脂、甲基丙烯酸乙酯于120～140℃温度下搅拌反应30～40min，过滤；所得滤液中加入己二烯酸，于20～30℃温度下搅拌混合均匀；加入多元醇和催化...