The invention provides a wood material and method for a flowerpot preparation method, by weight, is made of the following components: PVC resin powder 100 parts, glass fiber 60 80, 5 10 Hexadienoic acid, ammonium polyphosphate (APP) 5 10 copies, 8 mg of iron ore 10 a 5, caprolactam 8, 2 cerium oxide 3 copies, 1.5 copies, 1 main antioxidant auxiliary antioxidant 3 4 copies, 1 copies, 0.5 propylene oxide UV absorber UV P0.2 0.5, 1 copies of phytosterol. As a selection, the main antioxidant is 1010 antioxidant, and the auxiliary antioxidant is bisphenol C. The invention also provides a preparation method of the wood plastic material for the flowerpot. The combined preparation method of the above formula can solve the existing wood plastic material used as a flowerpot material, and there is a lack of ventilation, aging, cracking and other problems.
【技术实现步骤摘要】
一种花盆用木塑材料及其制备方法
技术介绍
花盆，种花用的一种器皿，为口大底端小的倒圆台或倒棱台形状。种植花卉的花盆形式多样，大小不一。花卉生产者或养花人士可以根据花卉的特性和需要以及花盆的特点选用花盆，根据制作材料不同，可以分为很多种。通常花盆是用质地为泥、瓷、塑料、石及木制品等材料制作的盆形容器，主要应用在园林绿化、景观绿化、私家园林、小区绿化。木塑材料，作为一种绿色环保材料，在该领域应用研究不多，所以现有的木塑材料作为花盆材料使用，存在疏水通气性不足、易老化、开裂等问题。
技术实现思路
本专利技术所要解决的技术问题在于提供一种花盆用木塑材料及其制备方法，能够解决现有的木塑材料作为花盆材料使用，存在的通气性不足、易老化、开裂等问题。为解决上述现有的技术问题，本专利技术采用如下方案：一种花盆用木塑材料，按重量份计，由以下组份制成：PVC树脂粉100份、玻璃纤维60-80份、己二烯酸5-10份、聚磷酸铵（APP）5-10份、镁铁矿石8-10份、己内酰胺5-8份、氧化铈2-3份、主抗氧化剂1-1.5份、辅抗氧剂3-4份、环氧丙烷0.5-1份、紫外线吸收剂UV-P0.2-0.5、...
【技术保护点】
一种花盆用木塑材料及其制备方法，其特征在于，按重量份计，由以下组份制成：PVC树脂粉100份、玻璃纤维60‑80份、己二烯酸5‑10份、聚磷酸铵（APP）5‑10份、镁铁矿石8‑10份、己内酰胺5‑8份、氧化铈2‑3份、主抗氧化剂1‑1.5份、辅抗氧剂3‑4份、环氧丙烷0.5‑1份、紫外线吸收剂UV‑P0.2‑0.5、植物甾醇1份；所述主抗氧化剂采用抗氧剂1010，辅抗氧剂采用双酚C；所述紫外线吸收剂UV‑P，主要成分是2‑（2ˊ‑羟基‑5ˊ‑甲基苯基）苯并三氮唑。
【技术特征摘要】
1.一种花盆用木塑材料及其制备方法，其特征在于，按重量份计，由以下组份制成：PVC树脂粉100份、玻璃纤维60-80份、己二烯酸5-10份、聚磷酸铵（APP）5-10份、镁铁矿石8-10份、己内酰胺5-8份、氧化铈2-3份、主抗氧化剂1-1.5份、辅抗氧剂3-4份、环氧丙烷0.5-1份、紫外线吸收剂UV-P0.2-0.5、植物甾醇1份；所述主抗氧化剂采用抗氧剂1010，辅抗氧剂采用双酚C；所述紫外线吸收剂UV-P，主要成分是2-（2ˊ-羟基-5ˊ-甲基苯基）苯并三氮唑。2.根据权利要求1所述的花盆用木塑材料的制备方法，其特征在于，包括以下步骤：（1）备料：将玻璃纤维在水中浸泡2小时后，使用单螺...