The present invention provides a kind of all steel radial tire shoulder pad rubber composition, in particular to a high performance of all steel radial tire shoulder pad rubber composition, the composition by weight consists of the following parts by weight of material: 100 parts of natural rubber, activating agent 2~8, curing agent 1.5 ~ 5, antioxidant 2~3 copies, 30~50 copies of the filler, coupling agent 1 to 3.5 parts, reaction type crosslinking agent 0.5 ~ 1.5, 0.1 ~ 0.3 antiscorcher. The high performance all steel radial tire shoulder pad has the advantages of low heat generation and good thermal stability, and improves the stability of the mechanical properties such as the stretching stress and tensile strength during the tire running, and improves the service life of the tire.
【技术实现步骤摘要】
全钢子午线轮胎胎肩垫胶组合物及其制备方法
本专利技术涉及一种全钢子午线轮胎胎肩垫胶组合物及其制备方法，属于橡胶轮胎
技术介绍
胎肩垫胶作为轮胎的心脏，肩部应力集中部位，在轮胎在行驶过程中，受长时间的形变和屈挠的下，肩部生热高，垫胶力学性能下降快，容易导致肩空等轮胎病象。因此需胎肩要垫胶具备生热低、耐屈挠性能好和高温下胶料的热稳定性好。为了保证胎肩垫胶的屈挠疲劳性能，胎肩垫胶大多采用高硫低促的硫化体系，而对于这种硫化体系形成的多硫键在轮胎高温行驶下热稳定差，一旦力学性能的下降，容易出现肩部应力的变化，容易出现肩空。为了提升轮胎质量，降低肩空，改善肩部垫胶的热稳定性和低生热性显得尤为重要。目前大多数轮胎企业采用提高防老剂用量和抗硫化返原剂来提升胎肩垫胶的热稳定性和降低返原问题，虽然有一定的效果，但是效果不明显，且成本高。为提高轮胎的使用寿命，提高胎肩垫胶的热稳定性和降低垫胶生热，成为了轮胎研发人员的一个重要课题。
技术实现思路
本专利技术的目的就是提供一种高性能全钢子午线轮胎胎肩垫胶橡胶组合物，所述的这种高性能全钢子午线轮胎胎肩垫胶橡胶组合物解决了轮胎胎肩垫胶生...
【技术保护点】
一种全钢子午线轮胎胎肩垫胶组合物，其特征在于，包括按重量份数计的如下组分：
【技术特征摘要】
1.一种全钢子午线轮胎胎肩垫胶组合物，其特征在于，包括按重量份数计的如下组分：2.如权利要求1所述的全钢子午线轮胎胎肩垫胶组合物，其特征在于，所述的填料为炭黑和白炭黑的混合物，其中炭黑的用量为10～35份，白炭黑的用量为15～30份；所述的偶联剂为双-[γ-(三乙氧基硅)丙基]四硫化物，用量为白炭黑重量份的10％～12％；所述的反应型交联剂为1,6-双(N,N′-二苯并噻唑氨基甲酰二硫)-己烷。3.如权利要求1或2所述的全钢子午线轮胎胎肩垫胶组合物，其特征在于，所述硫化剂为不溶性硫磺和促进剂的混合物，所述硫化剂与反应型交联剂的重量份数之和为2～6.5份。4.如权利要求1所述的全钢子午线轮胎胎肩垫胶组合物，其特征在于，所述促进剂为N-叔丁基-2-苯并噻唑次磺酰胺，所述防老剂选自N-(1，3-二甲基丁基)-N′-苯基对苯二胺、2，2，4-三甲基-1，2-二氢化喹啉聚合体中的一种或两种，所述防焦剂为N-环己基硫代邻苯二甲酰亚胺，所述活性剂为硬脂酸和氧化锌的混合物。5.一种如权利要求1所述的全钢子午线轮胎胎肩垫胶组合物的制备方法，其特征在于，包括：一段母炼胶的制备步骤；终炼的步骤。6.如权利要求5...
【专利技术属性】
技术研发人员：彭俊彪，王鹤元，
申请(专利权)人：上海豪元橡胶制品有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。