The invention discloses a water soluble ceramic core, including: 7 refractory aggregate, 14 parts by weight of 60 70 weight portions of salt and 24 28 parts by weight of a plasticizer, a surface water soluble ceramic core coated with a layer of waterproof membrane, the waterproof membrane comprises the following component: resin, 32 parts by weight of 3 by weight of the curing agent and 50 parts by weight of a solvent, which is preferably the resin, phenolic resin, curing agent, using six methyl four amine, preferably acetone solvent. The water-soluble ceramic core of the invention has a waterproof membrane on the surface, which can effectively resist the wetting of water vapor and ensure the surface quality of the core and the casting when the core is removed.
【技术实现步骤摘要】
一种水溶性陶瓷型芯及其制备方法
本专利技术涉及熔模铸造
，具体是一种水溶性陶瓷型芯及其制备方法。
技术介绍
金属铸造是将金属熔炼成符合一定要求的液体并浇进铸型里，经冷却凝固、清整处理后得到有预定形状、尺寸和性能的铸件的工艺过程。铸造毛胚因近乎成形，而达到免机械加工或少量加工的目的降低了成本并在一定程度上减少了时间．金属铸造是现代机械制造工业的基础工艺之一。陶瓷型芯是熔模铸造工艺中使用的一种陶瓷型芯的简称，作为形成铸件空腔的转接体，其作用是：形成铸件的内腔结构，与外型模及模壳共同保证铸件对空腔的尺寸精度要求。陶瓷型芯通常用于形成形状复杂或不易成形的铸件的型腔，作为简化工艺难度降低成本提高制品合格率的一种特殊的工艺手段。水溶型芯遇水溶解或溃散，其优点在于便于脱芯，但型芯在脱芯时会受到水溶液和水蒸气的浸蚀，寿命不高，对铸件表面粗糙度有不利影响。
技术实现思路
本专利技术的目的在于提供一种水溶性陶瓷型芯及其制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种水溶性陶瓷型芯，包括：7-14重量份的耐火骨料、60-70重量份的食盐和24...
【技术保护点】
一种水溶性陶瓷型芯，其特征在于：包括：7‑14重量份的耐火骨料、60‑70重量份的食盐和24‑28重量份的增塑剂，一种水溶性陶瓷型芯的表面涂覆一层防水膜，所述防水膜包括以下组分：32重量份的树脂、3重量份的固化剂和50重量份的溶剂，其中，树脂优选为酚醛树脂，固化剂采用六次甲基四胺，溶剂优选为丙酮。
【技术特征摘要】
1.一种水溶性陶瓷型芯，其特征在于：包括：7-14重量份的耐火骨料、60-70重量份的食盐和24-28重量份的增塑剂，一种水溶性陶瓷型芯的表面涂覆一层防水膜，所述防水膜包括以下组分：32重量份的树脂、3重量份的固化剂和50重量份的溶剂，其中，树脂优选为酚醛树脂，固化剂采用六次甲基四胺，溶剂优选为丙酮。2.根据权利要求1所述的一种水溶性陶瓷型芯，其特征在于：所述增塑剂优选为粗制聚乙二醇。3.根据权利要求1所述的一种水溶性陶瓷型芯，其特征在于：所述耐火骨料为120筛号电熔刚玉。4.根据权利要求1所述的一种水溶性陶瓷型芯，其特征在于：所述防水膜的成膜方法为：将树脂和固化剂加入到溶剂中，充分搅拌均匀，并自然风干，而后加热，在100℃条...
【专利技术属性】
技术研发人员：鲁茂波，
申请(专利权)人：东风精密铸造安徽有限公司，
类型：发明
国别省市：安徽,34