一种铝合金导线拉制工艺制造技术

本发明专利技术是一种铝合金导线拉制工艺，包括的如下步骤：1)铝合金导线的拉制在一般的拉丝机上进行，制的范围在10～0.12mm；2)金属拉丝机基本上分成两类:滑动式拉丝机和非滑动式拉丝机；3)拉制10.00～2.00mm线径的导线多采用非滑动式拉丝机，拉制2.00mm以下线径的导线采用滑动式拉丝机。本发明专利技术所述一种铝合金导线拉制工艺，保持电缆的优良传输性能，还能有效地降低原材料的消耗，可使成本下降40％左右。

A drawing process of aluminum alloy wire

The present invention relates to a Aluminum Alloy wire drawing process, which comprises the following steps: 1) drawing Aluminum Alloy wire drawing machine in general, was in the range of 10 ~ 0.12mm; 2) metal wire drawing machine is basically divided into two types: sliding type drawing machine and non slip drawing machine drawing; 3) 10 - wire 2.00mm wire diameter with non slip drawing machine, wire drawing 2.00mm wire diameter using sliding type drawing machine. The aluminum alloy wire drawing process of the invention maintains the excellent transmission performance of the cable, effectively reduces the consumption of raw materials, and reduces the cost by about 40%.

【技术实现步骤摘要】
一种铝合金导线拉制工艺
本专利技术涉及铝合金导线拉制领域，尤其涉及一种铝合金导线拉制工艺。
技术介绍
铝合金导线应用于电力架空传输线已有近六十年的历史。这种铝合金主要基于铝-镁-硅，由于具有额定载流量大，损耗小、安装及维修简单等优点，使铝合金架空导线得到了广泛的应用。本文将详细介绍应用于CATV电缆外导体编织的铝合金导线的拉制工艺。铝合金导线的制造工艺为：铸合金-浇铸及轧制成杆-固溶热处理-淬火-拉制-人工时效处理。为此，设计一种铝合金导线拉制工艺，解决以上问题。
技术实现思路
本专利技术为克服以上不足，提供一种铝合金导线拉制工艺，包括的如下步骤：1)铝合金导线的拉制在一般的拉丝机上进行，制的范围在10～0.12mm；2)金属拉丝机基本上分成两类:滑动式拉丝机和非滑动式拉丝机；3)拉制10.00～2.00mm线径的导线多采用非滑动式拉丝机，拉制2.00mm以下线径的导线采用滑动式拉丝机。进一步，所述拉丝机的拉丝速度一般在10～30m/s，即600～1800m/min。本专利技术的有益效果是：本专利技术所述一种铝合金导线拉制工艺，保持电缆的优良传输性能，还能有效地降低原材料的消耗，可使成本本文档来自技高网...

【技术保护点】
一种铝合金导线拉制工艺，其特征在于，包括的如下步骤：1)铝合金导线的拉制在一般的拉丝机上进行，制的范围在10～0.12mm；2)金属拉丝机基本上分成两类:滑动式拉丝机和非滑动式拉丝机；3)拉制10.00～2.00mm线径的导线多采用非滑动式拉丝机，拉制2.00mm以下线径的导线采用滑动式拉丝机。

【技术特征摘要】
1.一种铝合金导线拉制工艺，其特征在于，包括的如下步骤：1)铝合金导线的拉制在一般的拉丝机上进行，制的范围在10～0.12mm；2)金属拉丝机基本上分成两类:滑动式拉丝机和非滑动式拉丝机；3)拉制10.00～2.00...