一种重金属离子去除剂的制备方法技术
A method for the preparation of heavy metal ion remover
The invention provides a preparation method of heavy metal ion remover, which adopts waste hardened cement concrete as raw material, and the preparation method is primary crushing and pre burning, crushing and separating, ball milling activation, and separating powder and separating agent. It can effectively remove heavy metal ions from wastewater such as copper, zinc, chromium and nickel. The process has the advantages of fast speed, short reaction time, stable removal effect, and can be operated at room temperature. The technology application of hardened cement paste in the waste concrete is expanded to the field of heavy metal wastewater treatment. There is no problem of limiting dosage, which improves the efficiency of resource utilization of waste cement and improves the economic added value of waste cement.
【技术实现步骤摘要】
一种重金属离子去除剂的制备方法
本专利技术涉及废弃物资源化利用及重金属废水处理
，具体涉及一种基于废弃硬化水泥石的重金属废水去除剂、制备方法及应用。
技术介绍
在建筑物或构筑物的施工，装修、拆迁等建筑业活动中会产生大量的建筑垃圾，且随着我国基础设施的快速推进和城镇化速率的加快，建筑垃圾产生量持续增加。据统计城市垃圾中约有1/3为建筑垃圾；到2011年底其存量已超过20亿吨，且每年新增建筑垃圾超过3亿吨。由于大多数城市中建筑垃圾填埋厂选址不当或临时堆放，不仅造成了土地资源的大量浪费也存在极大的安全隐患。例如，2015年12月20日，广东省深圳市发生山体滑坡，滑坡覆盖面积约38万平方米，截止到2016年1月28日已发现遇难者73名，且仍有4名人员失联。国务院“12·20”山体滑坡事件灾害调查组经调查认定，与以往的山体滑坡性质不同，此次事故中原有山体并没有滑动，而是由堆放建筑垃圾的受纳厂中堆积过量且坡度过陡的堆填体失稳垮塌、滑动引起。同时，建筑垃圾在堆积和填埋过程中与周围环境中的水相互作用，其渗滤液会造成地表水或地下水的污染。废弃硬化水泥混凝土主要包括废弃硬化水泥...
【技术保护点】
一种重金属离子去除剂的制备方法，其特征在于，采用废弃硬化水泥混凝土为原料，经初碎及预烧、粉碎及分离、球磨活化、选粉分离得到重金属去除剂。
【技术特征摘要】
1.一种重金属离子去除剂的制备方法，其特征在于，采用废弃硬化水泥混凝土为原料，经初碎及预烧、粉碎及分离、球磨活化、选粉分离得到重金属去除剂。2.根据权利要求1所述重金属离子去除剂的制备方法，其特征在于，包括如下步骤：1）初碎及预烧；取废弃硬化水泥混凝土初碎，控制初碎颗粒大小方便预烧；在温度控制在380~400℃条件下锻烧30-45min，然后取出自然冷却至室温；2）粉碎及分离：将步骤1）经预烧、冷却后的废弃硬化水泥混凝土进行粉碎，然后将粗骨料与碎料进行分离；3）球磨活化：将步骤2）分离所得的碎料在球磨机中进行球磨处理得到吸附颗粒，控制粒度小于80μm；4）选粉和分离：将步骤3）得到...
【专利技术属性】
技术研发人员：刘东升，周丽新，陈昔勇，时建伟，吕利平，刘艳，
申请(专利权)人：长江师范学院，
类型：发明
国别省市：重庆,50