一种经过PVD表面处理的高速钢或硬质合金制造技术
A high speed steel or hard alloy treated by the surface of PVD
A high-speed steel or cemented carbide surface treated by PVD is characterized by including the substrate, the binding layer from the inside to outside and the N modulation layer and functional layer in sequence. Combined with the coating layer is AlCr, the thickness of 0.2 0.3um, Al and Cr AlCr coating of the molar ratio of 70 to 30; the modulation layer of the AlCr coating, the thickness of 0.16 0.20um, Al and Cr material AlCr coating ratio was 70: 30; the function layer for TiSi coating, the thickness of 0.05um, Ti and Si TiSi in the coating material weight ratio is 85: 15. The modulation layer and function layer of the N repeat in cycles, 4 = N = 6, N is a natural number. The total thickness of the film (+ + binding layer modulation layer function layer) for 1.04 1.8um.
【技术实现步骤摘要】
一种经过PVD表面处理的高速钢或硬质合金
本技术属于表面处理
，涉及一种高速钢或者硬质合金的表面处理技术，特别是涉及一种经过PVD表面处理的高速钢或硬质合金。
技术介绍
为了提高高速钢或者硬质合金的使用寿命，目前国内外常采用渗氮、渗金属、电镀、化学镀等方法来强化高速钢或者硬质合金的表面。但处理工艺存在一定程度的污染，并且硬度低。物理气相沉积(PVD，physicalVaporDeposition)是在现代物理、化学、材料学、电子学等多学科基础上发展起来的一门先进的工程技术。它是将靶材(所镀薄膜材料)在真空环境下，经过物理过程而沉积在衬底(需镀膜工件)表面的过程。使用物理气相沉积技术在廉价的金属材料表面制造硬质陶瓷涂层是近年来研究的热点，在工具和模具上已经取得了成功的应用，解决了刀具的磨损和耐高温问题。电弧离子镀和磁控溅射是PVD方法中最为常见的硬质陶瓷涂层的制造技术，目前刀具和模具上常用的TiN、CrN等涂层就是采用电弧离子镀技术制造的。但常规电弧离子镀制造的陶瓷涂层如TiN、CrN等其硬度只有渗氮的两倍，耐磨寿命有限，同时不具有润滑性能。在高速钢和硬质合金...
【技术保护点】
一种经过PVD表面处理的高速钢或硬质合金，其特征在于，包括基体、由内而外依附在基体表面的结合层和依次重复N个周期的调制层和功能层，所述的结合层为AlCr涂层，其厚度为0.2‑0.3um；所述的调制层为AlCr涂层，其厚度为0.16‑0.20um；所述的功能层为TiSi涂层，其厚度为0.05um；所述的依次重复N个周期的调制层和功能层中，4≤N≤6，N为自然数，结合层、调制层与功能层的总厚度为1.04‑1.8um。
【技术特征摘要】
1.一种经过PVD表面处理的高速钢或硬质合金，其特征在于，包括基体、由内而外依附在基体表面的结合层和依次重复N个周期的调制层和功能层，所述的结合层为AlCr涂层，其厚度为0.2-0.3um；所述的调制层为AlC...
【专利技术属性】
技术研发人员：吴伟亮，冯刚，梁海洋，
申请(专利权)人：苏州星蓝纳米技术有限公司，
类型：新型
国别省市：江苏,32