The invention discloses a light roof compressive environmental protection composite thermal insulation material, which consists of the following parts by weight: 20 ingredients 30 cement, 5 10 mica powder, 0.1 1 copies of 2 copies of 0.1 wetting agent, dispersing agent, thickening agent 0.5 4 copies, 12 copies of 5 flame retardant 5 agent, 9 insulation filler, 10 12 inorganic filler, 1 3 50 pigments, 60 parts of water. The invention has the advantages of light weight, high strength, small thermal conductivity, high compressive strength and good toughness, which is an ideal new thermal insulation material for roof, and can be made into roof insulation boards in factories for transportation and construction, and the breakage rate is low.
【技术实现步骤摘要】
一种轻质抗压屋顶环保型复合保温材料
本专利技术涉及一种轻质抗压屋顶环保型复合保温材料。
技术介绍
建筑物节能工作作为一项基本国策己日益受到各方面的重视。屋面是建筑物围护结构的一个重要组成部分，屋面的能耗损失达到围护结构总能耗的9%'""""'10%，且占顶层楼能耗的40%以上，因此屋面保温材料性能的优劣不可轻视。近年来，一些新型的屋面保温材料的研制成功缓解了屋面耗能的问题，如挤压或模压聚苯乙烯泡沫板、现浇硬质聚氨脂泡沫塑料等。但这类材料的缺点有二:一是抗压强度低，其10%压缩后的强度仅达0.15:MPa，不能直接承受上人屋面的冲击荷载，因而不宜用于上人屋面:二是成本较高，会增加屋面工程造价。而一些用废旧聚苯乙烯泡沫塑料制成的水泥聚苯板虽然成本低廉，但其抗压强度仍较低，为0.3:MPa，也不能直接用于上人屋面。
技术实现思路
本专利技术所要解决的技术问题是：提供一种轻质抗压屋顶环保型复合保温材料。为解决上述技术问题，本专利技术采用的技术方案是：一种轻质抗压屋顶环保型复合保温材料，由以下重量份数的成份组成：20-30份水泥，5-10份云母粉，0.1-1份润湿剂，0.1-2份分散剂，0.5-4份增稠剂，5-12份阻燃剂，5-9份保温填料，10-12份无机填料，1-3份颜料，50-60份水。所述保温填料包括木质纤维、硅藻土、开孔膨胀珍珠岩中的一种。所述颜料为金红石型钛白粉、锐钛矿型钛白粉或立德粉中的任意一种或几种。所述无机填料为云母粉、陶瓷粉、氢氧化铝、石英砂中的一种或几种。本专利技术的有益效果是：质量轻、强度高、导热系数小，抗压强度高，而且韧性较好，是一种较为理想的...
【技术保护点】
一种轻质抗压屋顶环保型复合保温材料，由以下重量份数的成份组成：20‑30份水泥，5‑10份云母粉，0.1‑1份润湿剂，0.1‑2份分散剂，0.5‑4份增稠剂，5‑12份阻燃剂，5‑9份保温填料，10‑12份无机填料，1‑3份颜料，50‑60份水。
【技术特征摘要】
1.一种轻质抗压屋顶环保型复合保温材料，由以下重量份数的成份组成：20-30份水泥，5-10份云母粉，0.1-1份润湿剂，0.1-2份分散剂，0.5-4份增稠剂，5-12份阻燃剂，5-9份保温填料，10-12份无机填料，1-3份颜料，50-60份水。2.根据权利要求1所述一种轻质抗压屋顶环保型复合保温材料，其特征在于：所述...
【专利技术属性】
技术研发人员：郑小明，
申请(专利权)人：绵阳旺通科技有限公司，
类型：发明
国别省市：四川,51