一种无机保温砂浆制造技术

本发明专利技术属于建筑材料领域，提出一种无机保温砂浆，原料按重量份比包括：水泥15‑25份，中砂15‑25份，消石灰5‑10份，自来水15‑25份，纯丙乳液15‑25份，EVB保温颗粒5‑10份，硫酸铝1‑5份，镁粉1‑5份，膨胀剂1‑5份，消泡剂1‑3份；所述的膨胀剂是高分子吸水树脂（SAP）；所述的消泡剂是有机硅消泡剂；材料成本低，施工工艺简单；无气泡无空鼓，保温性能好；耐久耐污，使用寿命长。

A kind of inorganic thermal insulation mortar

The invention belongs to the field of building materials, put forward a kind of inorganic insulation mortar, raw materials by weight: 15 cement 25, sand 15 lime 5 25 copies, 10 copies, 25 copies of the 15 tap water, pure acrylic emulsion 15 25, EVB 5 insulation particles 10, sulfuric acid 1 aluminum magnesium powder 1 5 copies, 5 copies, 5 copies of the 1 expansion agent, defoaming agent 1 3; the expansive agent is a water absorbent resin (SAP); the defoaming agent is silicone defoaming agent; low material cost, simple construction process; no bubble free hollowing, good insulation performance; durability resistant, long service life.

【技术实现步骤摘要】
一种无机保温砂浆
本专利技术属于建筑材料领域，具体涉及一种无机保温砂浆。
技术介绍
无机保温砂浆因其耐火性能可以达到A级，有着广泛的市场需求。但是，目前无机保温砂浆的造价普遍较高，适用范围有一定限制。
技术实现思路
为克服现有技术不足，本专利技术提出一种无机保温砂浆。技术方案1.一种无机保温砂浆，原料按重量份比包括：水泥15-25份，中砂15-25份，消石灰5-10份，自来水15-25份，纯丙乳液15-25份，EVB保温颗粒5-10份，硫酸铝1-5份，镁粉1-5份，膨胀剂1-5份，消泡剂1-3份。2.所述的膨胀剂是高分子吸水树脂（SAP）。3.所述的消泡剂是有机硅消泡剂。本专利技术的有益效果在于：1.材料成本低，施工工艺简单。2.无气泡无空鼓，保温性能好。3.耐久耐污，使用寿命长。具体实施方式下面对本专利技术的实施例作详细说明，本实施例在以本专利技术技术方案为前提下进行实施，给出了详细的实施方式和具体的操作过程，但本专利技术的保护范围不限于下述的实施例。实施例11.一种无机保温砂浆，原料按重量包括：水泥15Kg，中砂15Kg，消石灰5Kg，自来水15Kg，纯丙乳液15Kg，EVB保温颗粒本文档来自技高网...

【技术保护点】
一种无机保温砂浆，其特征在于，原料按重量份比包括：水泥15‑25份，中砂15‑25份，消石灰5‑10份，自来水15‑25份，纯丙乳液15‑25份，EVB保温颗粒5‑10份，硫酸铝1‑5份，镁粉1‑5份，膨胀剂1‑5份，消泡剂1‑3份。

【技术特征摘要】
1.一种无机保温砂浆，其特征在于，原料按重量份比包括：水泥15-25份，中砂15-25份，消石灰5-10份，自来水15-25份，纯丙乳液15-25份，EVB保温颗粒5-10份，硫酸铝1-5份，镁粉1-5份，...

【专利技术属性】
技术研发人员：杨军，
申请(专利权)人：桂林洁宇环保科技有限责任公司，
类型：发明
国别省市：广西,45