The invention relates to the use of asphalt paint a mining machine, belonging to the technical field of mining machinery, it is characterized by A and B components are prepared according to the weight ratio of 1:1 and A; the component prepared by the following raw materials according to the weight proportion: 1 E54 epoxy resin, 0.1 to 0.4 E42 epoxy resin, 0.15 to 0.5 portions of Lu turg's LA300 type modified C9 resin, 0.1 to 0.2, E 10P hankle glycidyl Versatate, 0.02 to 0.1 portions of fumed silica, 0.2 ~ 0.5 AB1600 superfine barium sulfate, 0.2 to 0.6 portions of talcum powder, 0.1 ~ 0.8 a silicon powder, 0.02 to 0.6 grams of Bi's BYK type 111 modified fatty acid ammonium; the B was prepared by the following raw materials according to the weight proportion: 20~30 modified polyamide, 0.3 to 0.8 portions of defoaming agent. The beneficial effect of the invention is that the anti-corrosion and anti aging properties are good.
【技术实现步骤摘要】
一种矿山机械用沥青涂料
本专利技术涉及矿山机械
，特别是涉及一种矿山机械用沥青涂料。
技术介绍
户外矿山机械设备，是指在户外作业，并专业从事采矿、选矿、探矿的机械。矿山机械设备一般用于处理矿石，使低品质矿石有利用价值。使有价值的矿物与脉石分离。包括探矿机械、采矿机械和选矿机械。由于户外矿山机械设备工作环境恶劣，而且与矿石打交道，设备表面的保护层容易遭受各种冲击而被损坏，例如飞石的撞击或其它工具的磕碰。进而导致设备被腐蚀，设备维护频率和难度较大。
技术实现思路
为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种矿山机械用沥青涂料。本专利技术的目的是通过以下技术方案来实现的：一种矿山机械用沥青涂料，其特征在于：由A组分和B组分按1:1的重量配比配制而成；所述A组分由以下原料按以下重量配比配制而成：1份E54环氧树脂，0.1～0.4份E42环氧树脂，0.15～0.5份吕特格公司的LA300型改性C9树脂，0.1～0.2份汉科公司的E-10P型叔碳酸缩水甘油酯，0.02～0.1份气相二氧化硅，0.2～0.5份AB1600型超细硫酸钡，0.2～0.6份滑石粉，0...
【技术保护点】
一种矿山机械用沥青涂料，其特征在于：由A组分和B组分按1:1的重量配比配制而成；所述A组分由以下原料按以下重量配比配制而成：1份E54环氧树脂，0.1～0.4份E42环氧树脂，0.15～0.5份吕特格公司的LA300型改性C9树脂，0.1～0.2份汉科公司的E‑10P型叔碳酸缩水甘油酯，0.02～0.1份气相二氧化硅，0.2～0.5份AB1600型超细硫酸钡，0.2～0.6份滑石粉，0.1～0.8份硅微粉，0.02～0.6份毕克公司的BYK‑111型改性脂肪酸铵；所述B组分由以下原料按以下重量配比配制而成：20～30份改性聚酰胺，0.3～0.8份消泡剂。
【技术特征摘要】
1.一种矿山机械用沥青涂料，其特征在于：由A组分和B组分按1:1的重量配比配制而成；所述A组分由以下原料按以下重量配比配制而成：1份E54环氧树脂，0.1～0.4份E42环氧树脂，0.15～0.5份吕特格公司的LA300型改性C9树脂，0.1～0.2份汉科公司的E-10P型叔碳酸缩水甘油酯，0.02～0.1份气相二氧化硅，0...