中密度板用固化粉末涂料及其制备方法技术

本发明专利技术属于涂料技术领域，具体涉及一种中密度板用固化粉末涂料及其制备方法。中密度板用固化粉末涂料由如下重量份数的原料制成：聚酯树脂35‑45份、环氧树脂35‑45份、流平剂0.8‑1.5份、安息香0.5‑1份、光亮剂0.7‑1.5份、颜填料15‑25份、固化促进剂0.3‑0.6份。本发明专利技术涂料可以有效替代油漆，减少液体涂料带来的挥发性物质的伤害，无毒、环保。

Curing powder coating for medium density plate and its preparation method

The invention belongs to the field of coating technology, in particular to a curing powder coating for medium density plate and a preparation method. Made of MDF with curing powder coating comprises the following raw materials in parts by weight: 35 polyester resin 45, epoxy resin 35 45, leveling agent 0.8 1.5 copies, 1 copies, 0.5 benzoin brightener 0.7 1.5 copies, 25 copies, 15 fillers 0.3 curing agent 0.6. The paint can effectively replace the paint, reduce the damage caused by the volatile substances brought by the liquid coating, non-toxic and environmentally friendly.

【技术实现步骤摘要】
中密度板用固化粉末涂料及其制备方法
本专利技术属于涂料
，具体涉及一种中密度板用固化粉末涂料及其制备方法。
技术介绍
装饰用中密度板通常表面需要喷涂油漆，但是油漆污染大，有挥发性溶剂有毒气体，不环保；此外烘干时间长、效率低。粉末涂料作为一种无溶剂的干粉涂料，烘干时间短，无溶剂气体污染，是一种替代油漆的优良材料，但是由于粉末涂料一般固化条件为：固化温度180℃-200℃、固化时间20-30分钟。在中密度板上无法使用，因此研究一种低温快速固化的粉末涂料可以用在中密度板上。
技术实现思路
本专利技术的目的是提供一种中密度板用固化粉末涂料，该涂料可以有效替代油漆，减少液体涂料带来的挥发性物质的伤害，无毒、环保；本专利技术同时提供了中密度板用固化粉末涂料的制备方法，科学合理、简单易行。本专利技术所述的中密度板用固化粉末涂料，由如下重量份数的原料制成：所述的聚酯树脂为羧基聚酯树脂。所述的环氧树脂为环氧当量在700-1000g/eq的环氧树脂。所述的流平剂为丙烯酸酯类粉末涂料用流平剂。所述的光亮剂为丙烯酸类光亮剂。所述的固化促进剂为咪唑类固化促进剂或咪唑啉类固化促进剂中的一种。所述的颜填料由钛白本文档来自技高网...

【技术保护点】
一种中密度板用固化粉末涂料，其特征在于由如下重量份数的原料制成：

【技术特征摘要】
1.一种中密度板用固化粉末涂料，其特征在于由如下重量份数的原料制成：2.根据权利要求1所述的中密度板用固化粉末涂料，其特征在于所述的聚酯树脂为羧基聚酯树脂。3.根据权利要求1所述的中密度板用固化粉末涂料，其特征在于所述的环氧树脂为环氧当量在700-1000g/eq的环氧树脂。4.根据权利要求1所述的中密度板用固化粉末涂料，其特征在于所述的流平剂为丙烯酸酯类粉末涂料用流平剂。5.根据权利要求1所述的中密度板用固化粉末涂料，其特征在于所述的光亮剂为丙烯酸类光亮剂。6.根据权利要求1所述的中密度板用固化粉末涂料，其特征在于所述的固化促进剂为咪唑类固化促进剂或咪唑啉类固化促...

【专利技术属性】
技术研发人员：王延刚，刘春信，焦淑元，张海瑜，冯智刚，张中超，王厚福，刘海英，
申请(专利权)人：山东瑞丰高分子材料股份有限公司，
类型：发明
国别省市：山东,37