The invention relates to a preparation method of polyester resin for weather resistant powder coating, relating to the technical field of outdoor powder coating production, in particular to the processing technology field of polyester resin for producing paint. The invention is mainly composed of polyol and polybasic acid and condensation, removal of water through the reaction and generate the esterification reactions constantly, so as to obtain certain degree of polymerization of polyester resin polymer. Polyester resin will be produced for the production of outdoor powder coating, can make the surface of the product has the advantages of high gloss and excellent resistance to weathering, the weather aging resistance test, qualified can reach 1600h.
【技术实现步骤摘要】
耐候型粉末涂料用聚酯树脂的制备方法
本专利技术涉及耐候性粉末涂料生产
，特别是生产涂料用的聚酯树脂的加工工艺
技术介绍
现有的采用聚酯树脂制成的粉末涂料用于室外使用的物件喷涂时，在自然条件下，一长般耐候性难以满足高标准要求，在耐人工气候老化性试验中，只能达到800h合格，无粉化、起泡、开裂、剥落等异常现象。
技术实现思路
本专利技术目的在于提出一种可用于生产耐候性强的粉末涂料的聚酯树脂的制备方法。本专利技术包括以下步骤：1、将反应釜温度升至80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧化锡；2、将反应釜温度按2-3℃/15分钟升温速率升至240℃，在240℃下反应100～120分钟；3、投入间苯二甲酸后在240℃下反应120～180分钟；4、在0.090～0.095mPa真空下进行缩聚反应180～240分钟；5、将反应釜降温至180～200℃加入三苯基膦，反应30±2分钟出料，出料，取得聚酯树脂；所述反应过程的各原料投料质量比为新戊二醇35～45份、三羟甲基丙烷1～3份、对苯二甲酸10～20份、间苯二甲酸50～70份、单丁基氧化锡0.2～0.5份、三苯基膦1～3份。本专利技术主要由多元醇与多元酸缩合而成，通过反应生成水的去除而使酯化反应不断进行，从而获得一定聚合度的高分子聚酯树脂。将本专利技术方法生产的聚酯树脂用于生产粉末涂料，可使产品表面具有高光泽和优越的户外耐候性等优点，在耐人工气候老化性试验中，可达到1600h合格。具体实施方式：一、称量（重量份）：分别称取新戊二醇35～45份、三羟甲基丙烷1～3份、对苯二甲酸10～20份、...
【技术保护点】
耐候型粉末涂料用聚酯树脂的制备方法，其特征在于包括以下步骤 ： 将反应釜温度升至 80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧 化锡 ； 将反应釜温度按 2‑3℃ /15 分钟升温速率升至 240℃，在 240℃下反应 100 ～ 120 分 钟 ； 投入间苯二甲酸后在 240℃下反应 120 ～ 180 分钟 ； 在 0.090 ～ 0.095mPa 真空下进行缩聚反应 180 ～ 240 分钟 ； 将反应釜降温至 180 ～ 200℃加入三苯基膦，反应 30±2 分钟出料，出料，取得聚酯 树脂 。
【技术特征摘要】
1.耐候型粉末涂料用聚酯树脂的制备方法，其特征在于包括以下步骤：将反应釜温度升至80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧化锡；将反应釜温度按2-3℃/15分钟升温速率升至240℃，在240℃下反应100～120分钟；投入间苯二甲酸后在240℃下反应120～180分钟；在0.090～0.0...
【专利技术属性】
技术研发人员：谢海，
申请(专利权)人：江苏冠军涂料科技集团有限公司，
类型：发明
国别省市：江苏,32