The invention discloses a method for weathering steel bridge structure, the high strength weathering steel including C:0.01 0.06wt%, Si:0.12 0.25wt%, Mn:0.7 1.3wt%, P:0.005 0.02wt%, S:0.002 0.005wt%, Cu:0.1 0.8wt%, Ti:0.06 0.79wt%, Nb:0.035 0.052wt%, V:0.025 0.080wt%, Als:0.015 0.060wt%, residual iron and impurities. The invention of the weathering steel has good corrosion resistance, while the application of weathering steel pre investment costs than carbon steel is slightly higher, but compared with the carbon steel surface spray coating method, the maintenance cost is late Carbon Weathering Steel 1.5 2 times, at the same time, can reduce the environmental pollution.
【技术实现步骤摘要】
一种用于桥梁结构的耐候钢
本专利技术属于冶金领域，更具体地，涉及一种用于桥梁结构的耐候钢。
技术介绍
耐候钢，即耐大气腐蚀钢，是介于普通钢和不锈钢之间的低合金钢系列，耐候钢由普碳钢添加少量铜、镍等耐腐蚀元素而成，具有优质钢的强韧、塑延、成型、焊割、磨蚀、高温、抗疲劳等特性；耐候性为普碳钢的2-8倍，涂装性为普碳钢的1.5-10倍。同时，它具有耐锈，使构件抗腐蚀延寿、减薄降耗，省工节能等特点。耐候钢主要用于铁道、车辆、桥梁、塔架、光伏、高速工程等长期暴露在大气中使用的钢结构。用于制造集装箱、铁道车辆、石油井架、海港建筑、采油平台及化工石油设备中含硫化氢腐蚀介质的容器等结构件。与不锈钢相比，耐候钢只有微量的合金元素，诸如磷、铜、铬、镍、钼、铌、钒、钛等，合金元素总量仅占百分之几，而不像不锈钢那样，达到百分之十几，因此价格较为低廉。耐候钢一般采用精料入炉-冶炼(转炉、电炉-微合金化处理-吹氩-LF精炼-低过热度连铸(喂入稀土丝)-控轧控冷等工艺路线。在冶炼时，废钢随炉料一起加入炉内，按常规工艺冶炼，出钢后加入脱氧剂及合金，钢水经吹氩处理后，随即进行浇铸，吹氩调温后的钢水...
【技术保护点】
一种用于桥梁结构的耐候钢，其特征在于，该高强耐候钢包括C：0.01‑0.06wt％、Si：0.12‑0.25wt％、Mn：0.7‑1.3wt％、P：0.005‑0.02wt％、S：0.002‑0.005wt％、Cu：0.1‑0.8wt％、Ti：0.06‑0.79wt％、Nb：0.035‑0.052wt％，V：0.025‑0.080wt％、Als：0.015‑0.060wt％，余量为铁和杂质。
【技术特征摘要】
1.一种用于桥梁结构的耐候钢，其特征在于，该高强耐候钢包括C：0.01-0.06wt％、Si：0.12-0.25wt％、Mn：0.7-1.3wt％、P：0.005-0.02wt％、S：0.002-0.005wt％、Cu：0.1-0.8wt％、Ti：0.06-0.79wt％、Nb：0.035-0.052wt％，V：0.025-0.080wt％、Als：0.015-0.060wt％，余量为铁和杂质。2.根据权利要求1所述的一种用于桥梁结构的耐候钢，其中，所述耐候钢还包括Cr：0.1-0.5wt％。3.根据权利要求1所述的一种用于桥梁结构的耐候钢，其中，所述耐候钢还包括Cr：0.4-0.5wt％。4.根据权利要求1所述的一种用于桥梁结构的...
【专利技术属性】
技术研发人员：陈辰，黄海峰，杨明，
申请(专利权)人：芜湖铁路桥梁制造有限公司，
类型：发明
国别省市：安徽,34