The present invention relates to a PE/ABS alloy material, which comprises the following raw materials by weight: PE 25 50; ABS 8 30; PMMA 2 15; PVC3 9; 2 compatibilizer 8; antioxidant 1 3; 1 5 toughening agent 1; lubricant 3, anti-aging agent 1 3. Compared with the prior art, the invention has the beneficial effects: the addition of PMMA and amount of PVC in PE alloy and ABS and with the addition of compatibilizer, heat stabilizer, toughening agent and anti-aging agent, can obtain a good weather resistance, high strength and high corrosion resistance of the alloy material, especially suitable for outdoor application, such as cables, pipes etc..
【技术实现步骤摘要】
一种PE/ABS合金材料及其制备方法
本专利技术属于新材料领域，具体涉及一种PE/ABS合金材料及其制备方法。
技术介绍
聚乙烯(PE)是五大合成树脂之一，是我国合成树脂中产能最大、进口量最多的品种。聚乙烯主要分为线性低密度聚乙烯(LLDPE)、低密度聚乙烯(LDPE)、高密度聚乙烯(HDPE)三大类。HDPE是一种结晶度高、非极性的热塑性树脂。原态HDPE的外表呈乳白色，在微薄截面呈一定程度的半透明状。PE具有优良的耐大多数生活和工业用化学品的特性。某些种类的化学品会产生化学腐蚀，例如腐蚀性氧化剂(浓硝酸)，芳香烃(二甲苯)和卤化烃(四氯化碳)。该聚合物不吸湿并具有好的防水蒸汽性，可用于包装用途。HDPE具有很好的电性能，特别是绝缘介电强度高，使其很适用于电线电缆。中到高分子量等级具有极好的抗冲击性，在常温甚至在-40F低温度下均如此。各种等级HDPE的独有特性是四种基本变量的适当结合：密度、分子量、分子量分布和添加剂。不同的催化剂被用于生产定制特殊性能聚合物。这些变量相结合生产出不同用途的HDPE品级；在性能上达到最佳的平衡。ABS树脂是五大合成树脂之一，其抗...
【技术保护点】
一种PE/ABS合金材料，其特征在于，包括如下重量份数的各原料：PE 25‑50份；ABS 8‑30份；PMMA 2‑15份；PVC3‑9份；相容剂2‑8份；热稳定剂1‑3份；增韧剂1‑5份；润滑剂1‑3份、抗老化剂1‑3份。
【技术特征摘要】
1.一种PE/ABS合金材料，其特征在于，包括如下重量份数的各原料：PE25-50份；ABS8-30份；PMMA2-15份；PVC3-9份；相容剂2-8份；热稳定剂1-3份；增韧剂1-5份；润滑剂1-3份、抗老化剂1-3份。2.根据权利要求1所述的一种PE/ABS合金材料，其特征在于，包括如下重量份数的各原料：PE42份；ABS12份；PMMA8份；PVC6份；相容剂6份；热稳定剂2份；增韧剂3份；润滑剂1份、抗老化剂2份。3.根据权利要求1所述的一种PE/ABS合金材料，其特征在于，所述相容剂为PP-g-MA、PP-g-...
【专利技术属性】
技术研发人员：郑波，何星基，何星存，
申请(专利权)人：桂林奥尼斯特节能环保科技有限责任公司，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。