一种超高分子量聚乙烯/高岭土复合材料及其制备方法技术

本发明专利技术公开了一种超高分子量聚乙烯/高岭土复合材料，属于高分子材料领域，所述复合材料由100‑120份超高分子量聚乙烯、6‑13份高岭土、0.3‑1.5份硅烷偶联剂组成。本发明专利技术在超高分子量聚乙烯中添加高岭土和硅烷偶联剂，制备的复合材料具有优异的综合性能,加工成型尺寸稳定性好,耐磨耗性好,温度使用范围广,可用作受力部件和轴承、齿轮等精密度要求高的机械部件。

A kind of ultra-high molecular weight polyethylene / kaolin composite and its preparation method

The invention discloses a UHMWPE / kaolin composite material, belonging to the field of polymer materials, the composite material is composed of 100 120 ultra high molecular weight polyethylene, 6 13 copies, 1.5 copies of 0.3 kaolin silane coupling agent composition. The addition of kaolin and silane coupling agent in the ultra high molecular weight polyethylene, the composite has excellent comprehensive properties, forming good dimensional stability, good abrasion resistance, the use of a wide range of temperature, can be used as stress components and bearings and gear precision for high mechanical components.

【技术实现步骤摘要】
一种超高分子量聚乙烯/高岭土复合材料及其制备方法
本专利技术属于高分子材料领域，具体涉及一种超高分子量聚乙烯/高岭土复合材料及其制备方法。
技术介绍
聚乙烯是应用最广泛也是产量最大的合成树脂之一，主要应用于工农业生产及人类生活的各个方面。聚乙烯种类繁多，按照分子量的不同可以分为：低分子量聚乙烯、普通分子量聚乙烯和超高分子量聚乙烯。超高分子量聚乙烯是一种分子量在150万以上的、线性结构的、具有优异的耐摩擦性、耐冲击性、自润滑性、耐化学药品性、耐低温、卫生无毒、拉伸强度高等性能的热塑性工程塑料。在以超高分子量聚乙烯为基体制备复合材料时，一般是通过将超高分子量聚乙烯、填料和加工助剂混合，经过热压成型形成复合材料。目前，市场上的超高分子量聚乙烯复合材料存在硬度、摩擦磨损性不佳或者常因高温变形而失效等问题。因此，如何改善超高分子量聚乙烯复合材料的综合性能是研究的关键。
技术实现思路
本专利技术的目的是提供一种尺寸稳定性、热变形温度和硬度较高的超高分子量聚乙烯/高岭土复合材料及其制备方法。为了实现本专利技术的目的，采用如下技术方案：一种超高分子量聚乙烯/高岭土复合材料，所述复合材料由100-120份本文档来自技高网...

【技术保护点】
一种超高分子量聚乙烯/高岭土复合材料，其特征在于，所述复合材料由100‑120份超高分子量聚乙烯、6‑13份高岭土、0.3‑1.5份硅烷偶联剂组成。

【技术特征摘要】
1.一种超高分子量聚乙烯/高岭土复合材料，其特征在于，所述复合材料由100-120份超高分子量聚乙烯、6-13份高岭土、0.3-1.5份硅烷偶联剂组成。2.根据权利要求1所述的超高分子量聚乙烯/高岭土复合材料，其特征在于，所述复合材料由100-110份超高分子量聚乙烯、6-10份高岭土、0.3-1.2份硅烷偶联剂组成。3.根据权利要求2所述的超高分子量聚乙烯/高岭土复合材料，其特征在于，所述复合材料由100份超高分子量聚乙烯、6份高岭土、0.5份硅烷偶联剂组成。4.根据权利要求1-3任一项所述的超高分子量聚乙烯/高岭土复合材料，其特征在于，超高分子量聚乙烯的相对分子量为250万-300万。5.一种超高分子量聚乙烯/高岭土复合材料的制备方法...

【专利技术属性】
技术研发人员：方庆忠，叶院林，
申请(专利权)人：中玺新材料安徽有限公司，
类型：发明
国别省市：安徽,34