The invention discloses a preparation method of modified UHMWPE Composite material, belonging to the field of polymer materials, composite material consisting of 80 120 ultra high molecular weight polyethylene, 7 12, 5 10 nano silica glass beads, 0.1 0.8 silane coupling agent. The present invention in the ultra high molecular weight polyethylene add nano silica and glass beads, nano silica particles and glass beads can block the furrow and the expansion of the plastic deformation, prevent abrasive embedding and cutting. Proper amount of nano silica particles can improve the friction and wear resistance and erosion resistance of ultra-high molecular weight polyethylene, while glass bead can improve the thermal stability and friction and creep properties of ultra-high molecular weight polyethylene to a certain extent.
【技术实现步骤摘要】
一种改性超高分子量聚乙烯复合材料的制备方法
本专利技术属于高分子材料领域，具体涉及一种改性超高分子量聚乙烯复合材料的制备方法。
技术介绍
聚乙烯是应用最广泛也是产量最大的合成树脂之一，主要应用于工农业生产及人类生活的各个方面。聚乙烯种类繁多，按照分子量的不同可以分为：低分子量聚乙烯、普通分子量聚乙烯和超高分子量聚乙烯。超高分子量聚乙烯是一种分子量在150万以上的、线性结构的、具有优异的耐摩擦性、耐冲击性、自润滑性、耐化学药品性、耐低温、卫生无毒、拉伸强度高等性能的热塑性工程塑料，在工业、农业、医疗、建筑、化工和国防等领域应用广泛，但其表面硬度低、热变形温度低、抗磨粒磨损和抗疲劳磨损性能差。
技术实现思路
本专利技术的目的是提供一种耐磨性能、表面硬度高的改性超高分子量聚乙烯复合材料及其制备方法。为了实现本专利技术的目的，采用如下技术方案：一种改性超高分子量聚乙烯复合材料的制备方法，包括以下步骤:(1)将纳米二氧化硅和玻璃微珠恒温干燥至恒重，然后称重；(2)将硅烷偶联剂用无水乙醇稀释，并与纳米二氧化硅、玻璃微珠混合搅拌均匀，然后在超声波震荡仪中震荡分散30-40min，在...
【技术保护点】
一种改性超高分子量聚乙烯复合材料的制备方法，其特征在于，所述复合材料80‑120份超高分子量聚乙烯、7‑12份纳米二氧化硅、5‑10份玻璃微珠、0.1‑0.8份硅烷偶联剂组成,包括以下步骤:(1)将纳米二氧化硅和玻璃微珠恒温干燥至恒重，然后称重；(2)将硅烷偶联剂用无水乙醇稀释，并与纳米二氧化硅、玻璃微珠混合搅拌均匀，然后在超声波震荡仪中震荡分散30‑40min，在烘干至恒重，研磨；(3)将步骤(2)制备的混合物与超高分子量聚乙烯混合，放入多向运动混料机中混料8‑12h；(4)将步骤(3)制备的混料放入模具中，对模具进行预压，使模具内的混合料分布更均匀；(5)将模具逐渐加热...
【技术特征摘要】
1.一种改性超高分子量聚乙烯复合材料的制备方法，其特征在于，所述复合材料80-120份超高分子量聚乙烯、7-12份纳米二氧化硅、5-10份玻璃微珠、0.1-0.8份硅烷偶联剂组成,包括以下步骤:(1)将纳米二氧化硅和玻璃微珠恒温干燥至恒重，然后称重；(2)将硅烷偶联剂用无水乙醇稀释，并与纳米二氧化硅、玻璃微珠混合搅拌均匀，然后在超声波震荡仪中震荡分散30-40min，在烘干至恒重，研磨；(3)将步骤(2)制备的混合物与超高分子量...
【专利技术属性】
技术研发人员：方庆忠，叶院林，
申请(专利权)人：中玺新材料安徽有限公司，
类型：发明
国别省市：安徽,34