The invention relates to a process for the preparation of large size zinc sulfate, which comprises the following steps: (1) the concentrated Po Mido is zinc sulfate sample solution is placed on the mold of 54Be, the solution temperature of 50 DEG C to slow cooling to 30~34 DEG, a small crystal began to appear; (2) then the solution to 45 rapid heating to 48 DEG C, the crystal is completely dissolved, stirring rate of 70 /min; (3) the solution is slowly cooled to 39.5 DEG C to 40 DEG C, adding 3 4G seed, the rapid cooling solution to 25 29 DEG C, the cooling rate is 1 DEG /min, then the solution is constant 6h ~ 7h, stirring speed to 100 /min, zinc sulfate crystal large size appeared. The invention can obtain zinc sulfate with large particles, shorten the crystallization time and improve the production efficiency.
【技术实现步骤摘要】
一种制备大粒径硫酸锌的工艺
本专利技术属于一种锌的化合物的制备方法，尤其涉及一种制备大粒径硫酸锌的工艺。
技术介绍
硫酸锌是制造锌钡白和锌盐的主要原料，也可用作印染媒染剂，木材和皮革的保存剂，也是生产粘胶纤维和维尼纶纤维的重要辅助原料。另外，在电镀和电解工业中也有应用，还可以用于制造电缆。工业中冷却用水是最大用量水。在密闭式循环冷却系统中的冷却水对金属不能有腐蚀和结垢，因此要进行处理，这个过程就叫水质稳定，硫酸锌在此用作水质稳定剂。但是现在实际的生产中结晶时间长达十几个小时，结晶时间不够会使得到的产品颗粒细小，因其比表面积大而携带有部分游离水，工业生产中难于离心甩干，导致主品位锌含量不够且容易结块。
技术实现思路
本专利技术的目的在于提供一种制备大粒径硫酸锌的工艺。本专利技术可获得大颗粒的硫酸锌，缩短了结晶时间，提高了生产效率。本专利技术采用的技术方案：一种制备大粒径硫酸锌的工艺，包括以下步骤：(1)将浓缩的婆美度为54Be的硫酸锌样品溶液置于结晶器中，将溶液温度50℃开始缓慢降温到30～34℃时，有细小的晶体开始出现；(2)再将溶液快速升温到45-48℃，至晶体完全...
【技术保护点】
一种制备大粒径硫酸锌的工艺，其特征在于包括以下步骤：(1)将浓缩的婆美度为54Be的硫酸锌样品溶液置于结晶器中，将溶液温度50℃开始缓慢降温到30～34℃时，有细小的晶体开始出现；(2)再将溶液快速升温到45‑48℃，至晶体完全溶解，搅拌速率70转/min；(3)再将溶液缓慢降温到39.5℃～40℃时，加入3‑4g晶种，将溶液快速降温到25‑29℃，降温速率为1℃/min，再将溶液恒温6h～7h，搅拌转速调至100转/min、有大粒径的硫酸锌晶体出现。
【技术特征摘要】
1.一种制备大粒径硫酸锌的工艺，其特征在于包括以下步骤：(1)将浓缩的婆美度为54Be的硫酸锌样品溶液置于结晶器中，将溶液温度50℃开始缓慢降温到30～34℃时，有细小的晶体开始出现；(2)再将溶液快速升温到45-48℃，至晶体完...
【专利技术属性】
技术研发人员：高华勇，李文杰，
申请(专利权)人：侯马高知新生物科技有限公司，
类型：发明
国别省市：山西,14