The invention discloses a preparation method of high purity graphite, specifically the leaching process for producing high purity graphite thermal activation relates to a combined two acid, which comprises the following steps: Graphite rolling and grinding; a mixed acid leaching acid impregnated graphite formed in hydrofluoric acid and sulfuric acid in the heat; activation: to filter out graphite mixed acid, thermal activation treatment; two acid leaching: thermal activation treatment is completed, after cooling graphite two times leaching, mixed acid of the two acid leaching solution for hydrofluoric acid and sulfuric acid; filtering graphite solution from the acid washing and drying. The purity of graphite purified by this method is more than 99.99%.
【技术实现步骤摘要】
一种二次酸浸结合热活化制备高纯度石墨的方法
本专利技术涉及一种石墨提纯方法，具体涉及一种采用二次酸浸结合热活化制备高纯度石墨的方法。
技术介绍
石墨是碳质元素的结晶矿物，由于其优良的导电性、导热性、可塑性、润滑性、耐高温性而被广泛应用于冶金、化工、石油、机械、国防尖端技术、航空业、轻工业等众多领域。在冶金业中石墨主要作为耐火材料；在化工行业中石墨主要用作生产电池、电极以及各类碳素制品的原材料；在石油领域石墨烯的问世和迅猛发展，加快了后石油时代的发展，解决了巨大的能源问题；在机械领域中石墨主要用作各种结构零件的碳—石墨材料；在国防尖端技术中石墨可作为原子反应堆的中子减速剂和防护材料；在航空业中石墨用作导弹和火箭的隔热、耐热材料以及无线电连接信号和导电结构的材料；在轻工业中石墨是用作制造铅笔、墨汁、油墨和人造金刚石的原料，也作为造纸和玻璃防锈剂和磨光剂。随着现代工业以及现代科学技术的发展，石墨已经更加广泛的应用于其他各个领域，但这些行业需要的石墨中的固定碳含量高达99.9%以上，目前经过天然开采通过选矿处理的石墨中的碳含量最高可达95%，难以满足国民生产的要求。因此提...
【技术保护点】
一种二次酸浸结合热活化制备高纯度石墨的方法，其特征在于：包括以下步骤S01 将石墨碾压和粉碎；S02 一次酸浸：将石墨浸渍在氢氟酸和硫酸形成的混合酸中；S03 热活化处理：混合酸中过滤出石墨，进行热活化处理；S04 二次酸浸：热活化处理完毕，冷却后将石墨进行二次酸浸，所述二次酸浸溶液为氢氟酸和硫酸的混合酸；S05从酸浸溶液中过滤出石墨，洗涤干燥制得。
【技术特征摘要】
1.一种二次酸浸结合热活化制备高纯度石墨的方法，其特征在于：包括以下步骤S01将石墨碾压和粉碎；S02一次酸浸：将石墨浸渍在氢氟酸和硫酸形成的混合酸中；S03热活化处理：混合酸中过滤出石墨，进行热活化处理；S04二次酸浸：热活化处理完毕，冷却后将石墨进行二次酸浸，所述二次酸浸溶液为氢氟酸和硫酸的混合酸；S05从酸浸溶液中过滤出石墨，洗涤干燥制得。2.根据权利要求1所述的制备方法，其特征在于：所述步骤S02中一次酸浸的混合酸中氢氟酸浓度为5%~10%，硫酸浓度为30%~50%。3.根据权利要求1或2所述的制备方法，其特征在于：所述一次酸浸温度为70℃~75℃，酸浸时间为2h~4h。4....