等截面薄壁轴承零件的成型加工新工艺制造技术
New forming process of thin wall bearing parts with equal section
The present invention discloses a new forming process of processing with thin wall bearing parts, the technical scheme is: firstly, increase strength before heat treatment of bearing parts, bearing parts two into one, then the flange bearing parts of the corresponding connection, meet the bearing parts of the symmetry of the bearing deformation after heat treatment parts of the heat treatment is reduced, then the conventional process and bearing parts of the monomer, two pieces of bearing parts finally after heat treatment by cutting wheel cut in bearing grinder, the formation of two monomer bearing parts. The invention adopts two parts of bearing parts to integrate into one body, and the corresponding structural form of bearing parts flange is combined back to back, which solves the problem of large deformation of flange structure of equal section and thin wall bearing.
【技术实现步骤摘要】
等截面薄壁轴承零件的成型加工新工艺
：本专利技术涉及一种薄壁轴承热处理工艺，特别是涉及一种等截面薄壁轴承零件的成型加工新工艺。
技术介绍
：众所周知，为充分发挥轴承钢材料的机械性能，需对高碳铬轴承钢的轴承零件进行热处理淬火和回火处理，由于轴承零件在810--840度的高温下进行热处理工序，必然会使轴承零件产生端面弯曲变形和内径、外径椭圆变形，薄壁轴承零件热处理后会加大其变形量，对法兰结构的薄壁轴承零件热处理后同样变形也很大，使得轴承法兰上安装孔的位置度超差，不能满足产品的安装要求。随着国民经济的不断发展，各行各业都在向体积小，重量轻的方向上发展，以满足结构紧凑，能量消耗少的主机要求。这就给整机包括轴承提出了更高的要求。等截面薄壁法兰结构的轴承是今后发展的趋势，薄壁法兰结构轴承的热处理变形问题，造成轴承法兰安装孔位置度超差，是轴承业内人士急需要解决的问题。
技术实现思路
：本专利技术所要解决的技术问题是：克服现有技术的不足，提供一种设计合理、减少热处理变形、减少加工余量且保证法兰上安装孔位置度的等截面薄壁轴承零件的成型加工新工艺。本专利技术的技术方案是：一种等截面薄壁轴...
【技术保护点】
一种等截面薄壁轴承零件的成型加工新工艺，其特征是：首先增大热处理前轴承零件的强度，将轴承零件两件合为一体，其次将轴承零件的法兰相对应连接，满足轴承零件的对称性，使热处理后轴承零件的变形减小，然后进行和单体的轴承零件一样的常规工艺的热处理，最后将经过热处理的两件轴承零件在轴承磨床上通过切割片砂轮切割开，形成两个单体的轴承零件。
【技术特征摘要】
1.一种等截面薄壁轴承零件的成型加工新工艺，其特征是：首先增大热处理前轴承零件的强度，将轴承零件两件合为一体，其次将轴承零件的法兰相对应连接，满足轴承零件的对称性，使热处理后轴承零件的变形减小，然后进行和单体的轴承零件一样的常规工艺的热处理，最后将经过热处理的两件轴承零件在轴承磨床上通过切割片砂轮切割开，形成两个单体...