The invention discloses a method, a preparation Oxythiomolybdate cobalt catalyst comprises the following steps: 5~10 g two cobalt chloride is added to the 50~100 mL water to prepare solution, then added into the solution of 8~11 g and 1~2 sodium molybdate g glycine, 60~70 DEG C water bath stirring for 10 to 50 minutes duration stir in 25 Deg. C and normal pressure slowly pass into the 0.5~6 L hydrogen sulfide gas, continue stirring for 10~20 minutes, will transfer the solution to the hot water in the reactor, the temperature of 180~260 DEG C, the reaction of 5~10 h, filtering to obtain a solid, washing with distilled water 3~5 times, 80 drying, to obtain a generation of sulfur cobalt molybdate photocatalyst. The advantage of the invention is that the obtained cobalt molybdenum thiomolybdate photocatalyst has uniform crystal structure, good dispersion and good catalytic effect.
【技术实现步骤摘要】
一种硫代钼酸钴光催化剂的制备方法
本专利技术涉及环境污染控制新材料领域，尤其涉及一种硫代钼酸钴光催化剂的制备方法。
技术介绍
随着科技的发展，来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康，寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点，目前已成为一种具有重要应用前景的新兴环境治理技术。近年来，新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容，其中具有表面等离子共振效应的光催化材料，因其独特的表面物理化学性质和高效的可见光光催化性能，成为研究的热点之一。但纳米颗粒物容易团聚，团聚后表面积大大减小，效果减弱。钼酸钴由于具有稳定的晶体结构，可应用于锂离子负极材料、超级电容器电极材料以及催化剂等，并呈现出了良好的电化学性能和催化活性，因此在能量存储和催化领域拥有广阔的应用前景。硫代钼酸钴经过是经过硫取代的钼酸钴，可以改善光催化效果。
技术实现思路
本专利技术的目的是为克服现有技术的不足，提供一种硫代钼酸钴光催化剂的制备方法。本专利技术采用的技术方案是依次包括如下步骤：将5~10g二氯化钴...
【技术保护点】
一种硫代钼酸钴光催化剂的制备方法，其特征是依次包括如下步骤：将5~10 g二氯化钴加入到50~100 mL水中配制成溶液，再向该溶液中加入8~11 g钼酸钠和1~2 g甘氨酸，60~70℃水浴中搅拌10～50分钟，持续搅拌中，25℃和常压条件下缓慢通入0.5~6 L硫化氢气体，继续搅拌10~20分钟后，将溶液转移至水热反应器中，180~260℃下，反应5~10 h，过滤得到固体，用蒸馏水洗涤3~5遍，80℃烘干，即得到一种硫代钼酸钴光催化剂。
【技术特征摘要】
1.一种硫代钼酸钴光催化剂的制备方法，其特征是依次包括如下步骤：将5~10g二氯化钴加入到50~100mL水中配制成溶液，再向该溶液中加入8~11g钼酸钠和1~2g甘氨酸，60~70℃水浴中搅拌10～50分钟，持续搅拌...
【专利技术属性】
技术研发人员：程昊，白大伟，郝光明，史智鹏，
申请(专利权)人：柳州若思纳米材料科技有限公司，广西科技大学，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。