一种磁性壳聚糖微球/氧化锌复合抗菌剂及其制备方法技术
A magnetic chitosan microsphere / Zinc Oxide compound antibacterial agent and its preparation method
The invention discloses a magnetic chitosan microsphere / Zinc Oxide compound antibacterial agent. A magnetic chitosan microsphere prepared by one-step precipitation method was used as a carrier. It was placed in Zn (Ac) 2. 2H2O solution and added a certain concentration of NaOH solution. The magnetic chitosan microsphere / Zinc Oxide composite antibacterial agent was obtained by chemical deposition. The surface of the compound antibacterial agent is loaded with a large number of nano granular Zinc Oxide, which has high inactivation rate and lasting effect for the bacteria in water, and has a magnetic convenience to recover.
【技术实现步骤摘要】
一种磁性壳聚糖微球/氧化锌复合抗菌剂及其制备方法
本专利技术属于材料制备及环境保护
，具体涉及一种磁性壳聚糖微球/氧化锌复合抗菌剂及其制备方法。
技术介绍
随着健康和环保意识的提高，人们越来越多地追求无毒、无害的抗菌材料和方式。与传统的水处理消毒剂相比，新型抗菌剂具有无化学物质残留、无消毒副产物、不产生耐药菌等优点，可以应用于饮用水水源净化、供水输配管网除菌、循环水系统除菌等领域，近年来迅速成为关注的热点。氧化锌(ZnO)是一种在光照和黑暗条件下均具有良好抗菌性能的无机抗菌剂，它往往被制备成粉末状以增大其表面积，提高抗菌效果。但因ZnO颗粒尺寸微小，在水中投放后难以回收，故在实际应用中须对其进行固定化。现有的载体存在负载量小、回收费时费力等问题，且载体本身是完全惰性的，无助于提高细菌去除率。壳聚糖是一种典型的生物大分子，含有多个活泼的羟基和氨基。这些活性基团的存在决定了壳聚糖具有良好的吸附和絮凝性能。现已有研究报道制备出磁性壳聚糖微球，因其比表面积大、易回收、可再生等优点，作为吸附剂在处理重金废水、印染废水、造纸废水、含酚废水和食品废水中有广泛的应用。壳聚糖...
【技术保护点】
一种磁性壳聚糖微球/氧化锌复合抗菌剂的制备方法，其特征在于，该方法采用一步沉淀法制备出磁性壳聚糖微球，将该磁性壳聚糖微球置于锌溶液中，并加入一定浓度的NaOH溶液，控制温度和搅拌条件，进行化学沉积反应，反应完成后，待溶液自然冷却，纯水清洗，95℃烘干，即得到磁性壳聚糖微球/氧化锌复合抗菌剂。
【技术特征摘要】
1.一种磁性壳聚糖微球/氧化锌复合抗菌剂的制备方法，其特征在于，该方法采用一步沉淀法制备出磁性壳聚糖微球，将该磁性壳聚糖微球置于锌溶液中，并加入一定浓度的NaOH溶液，控制温度和搅拌条件，进行化学沉积反应，反应完成后，待溶液自然冷却，纯水清洗，95℃烘干，即得到磁性壳聚糖微球/氧化锌复合抗菌剂。2.如权利要求1所述的方法，其特征在于，具体按下列步骤制备：(1)制备壳聚糖溶胶：称取适量脱乙酰度≥90％的壳聚糖粉末，溶于体积分数为1％的HCl溶液中，制成浓度为13.8mg/mL的壳聚糖溶胶；(2)配制铁溶液：称取适量FeCl3·6H2O和FeCl2·4H2O溶于水中，使得溶液中Fe3+浓度为1mol/L，Fe2+浓度为0.5mol/L；(3)壳聚糖溶胶与铁溶液混合：将壳聚糖溶胶和铁溶液以质量比2:1进行混合，磁力搅拌使其完全混匀；(4)一步沉淀法制备磁性壳聚糖微球：以25％的浓氨水为沉淀剂，将步骤(3)中的混合液用1mL针管滴入氨水中，可见有黑色微球生成。静置7h后...