本发明专利技术公开了一种低敏感综合型聚羧酸减水剂，所述的聚羧酸减水剂的组成和重量份数的原料组成：聚羧酸溶液30～60份、异戊烯基聚氧乙烯基醚20～30份、丙烯酸类聚羧酸减水剂30～70份、丙烯酸羟乙酯10～30份、保坍型聚羧酸减水剂40～90份和缓释型聚羧酸减水剂15～40份。能够达到减水率高、保坍性能好、掺量敏感性低的效果，同时生产成本大为降低。

A low sensitive and synthetic polycarboxylic acid water reducer

The invention discloses a low sensitive integrated type polycarboxylate superplasticizer, the polycarboxylate superplasticizer composition and weight of raw materials: polycarboxylic acid solution for 30 to 60 copies, isopentenyl polyoxyethylene ether 20 - 30, acrylic type polycarboxylate superplasticizer is 30 ~ 70, HEMA ethyl 10 - 30, slump type polycarboxylate superplasticizer 40 ~ 90 phr and slow-release poly carboxylic acid water reducing agent 15 ~ 40. It can achieve the effect of high water reduction rate, good slump protection performance and low dosage sensitivity, while the production cost is greatly reduced.

【技术实现步骤摘要】
一种低敏感综合型聚羧酸减水剂
本专利技术涉及一种低敏感综合型聚羧酸减水剂，属于混凝土外加剂

技术介绍
目前国内市场上出售的聚羧酸减水剂主要有高减水型和保坍型两类。高减水型的聚羧酸减水剂由于具有较高的减水率，其掺量比较敏感，且混凝土流动度损失较快，给实际工程应用带来了一定的难度。保坍型聚羧酸减水剂保坍性能较好，但减水率一般比较低，通常要与减水剂复配使用，不适用于特殊要求的高性能混凝土。对于减水率高、保坍性能好、掺量敏感性低的综合型聚羧酸减水剂的合成目前国内较少，具有相似功能的聚羧酸减水剂的使用主要靠进口供应，因此成本高，不经济。
技术实现思路
针对上述现有技术存在的问题，本专利技术提供一种低敏感综合型聚羧酸减水剂，减水率、保坍性以及掺量敏感性等均高于市售产品，且成本远低于市售产品。为了实现上述目的，本专利技术采用的技术方案是：一种低敏感综合型聚羧酸减水剂，所述的减水剂的组成和重量份数为聚羧酸溶液份、异戊烯基聚氧乙烯基醚份、丙烯酸类聚羧酸减水剂份、丙烯酸羟乙酯份、保坍型聚羧酸减水剂份和缓释型聚羧酸减水剂份。进一步，所述的聚羧酸溶液由以下重量份数的原料组成：脂肪醇聚氧乙烯醚份，丙烯酸本文档来自技高网...

【技术保护点】
一种低敏感综合型聚羧酸减水剂，其特征在于，所述聚羧酸减水剂由以下重量份数的原料组成：聚羧酸溶液

【技术特征摘要】
1.一种低敏感综合型聚羧酸减水剂，其特征在于，所述聚羧酸减水剂由以下重量份数的原料组成：聚羧酸溶液异戊烯基聚氧乙烯基醚丙烯酸类聚羧酸减水剂丙烯酸羟乙酯保坍型聚羧酸减水剂和缓释型聚羧酸减水剂2.根据权利要求1所述的一种低敏感综合型聚羧酸减水剂，其特征在于，所述的聚羧酸溶液由以下重量份数的原料组成：脂肪醇聚氧乙烯醚丙烯酸双氧水催化剂和3.根据权利要求1-2任一所述的一种低敏感综合型聚羧酸减水剂，其特征在于，所述的保坍型聚羧酸减水剂包括以下重量份数的原...

【专利技术属性】
技术研发人员：崔松，
申请(专利权)人：江苏兆佳建材科技有限公司，
类型：发明
国别省市：江苏,32