The invention relates to a rod, in particular to an anti - dip rod, which belongs to the field of mechanical materials. The anti roll bar made of Aluminum Alloy materials, the Aluminum Alloy material consists of the following components: Mg:2.5 mass percentage 3.5%, Si:1.5 2%, Mn:0.5 1.5%, Zn:0.5 1%, Cu:0.3 0.8%, Yb:0.1 0.5%, Cr:0.1 0.5%, allowance for Al and inevitable impurity elements. The invention adopts the anti roll bar Aluminum Alloy material prepared by heat treatment, solid solution treatment, aging treatment and two-stage regression short-time high temperature treatment, while using anionic surfactant modified silane on Aluminum Alloy surface treatment, the invention makes anti roll bar with high strength and good stress corrosion resistance.
【技术实现步骤摘要】
一种防倾杆专利
本专利技术涉及一种杆件，具体涉及一种防倾杆，属于机械材料领域。
技术介绍
杆件，是指纵向(长度方向)尺寸比横向(垂直于长度方向)尺寸要大得多的构件。杆件的形状和尺寸可由杆的横截面和轴线两个主要几何元素来描述。横截面是指与杆长方向垂直的截面，而轴线是各横截面中心的连线。横截面与杆轴线是互相垂直的。轴线为直线、横截面相同的杆称为等截面直杆。汽车在高速转弯时，由于受到离心力的影响，车辆会产生倾轧，甚至侧翻，车辆容易失控，甚至会发生车毁人亡的事故。现代汽车为防止汽车发生倾轧，一般都装有防倾杆，但防倾杆如果强度不足，则其作用不能充分发挥，汽车倾轧现象依然存在。
技术实现思路
本专利技术针对现有技术存在的上述问题，提出了一种强度高、使用寿命长的防倾杆。本专利技术的上述目的可通过下列技术方案来实现：一种防倾杆，该防倾杆采用铝合金材料制成，所述铝合金材料由以下质量百分比的成分组成：Mg：2.5-3.5％，Si：1.5-2.0％，Mn：0.5-1.5％，Zn：0.5-1.0％，Cu：0.3-0.8％，Yb：0.1-0.5％，Cr：0.1-0.5％，余量为Al以及不可避免...
【技术保护点】
一种防倾杆，其特征在于，所述防倾杆采用铝合金材料制成，所述铝合金材料由以下质量百分比的成分组成：Mg：2.5‑3.5％，Si：1.5‑2.0％，Mn：0.5‑1.5％，Zn：0.5‑1.0％，Cu：0.3‑0.8％，Yb：0.1‑0.5％，Cr：0.1‑0.5％，余量为Al以及不可避免的杂质元素。
【技术特征摘要】
1.一种防倾杆，其特征在于，所述防倾杆采用铝合金材料制成，所述铝合金材料由以下质量百分比的成分组成：Mg：2.5-3.5％，Si：1.5-2.0％，Mn：0.5-1.5％，Zn：0.5-1.0％，Cu：0.3-0.8％，Yb：0.1-0.5％，Cr：0.1-0.5％，余量为Al以及不可避免的杂质元素。2.一种如权利要求1所述的防倾杆的制备方法，其特征在于，所述制备方法包括如下步骤：将制备防倾杆的铝合金材料进行熔炼，熔炼的同时加入覆盖剂，并用铁耙反复搅动使其完全熔化，得铝液；将铝液精炼后降温浇铸得防倾杆铸件；将防倾杆铸件进行热处理、硅烷化处理后得防倾杆成品。3.根据权利要求2所述的一种防倾杆的制备方法，其特征在于，所述覆盖剂的质量为铝合金材料质量的0.3-0.5％，所述覆盖剂包括如下质量百分比的组分：40-50％KCl，40-50％NaCl，10-20％冰晶石。4.根据权利要求2所述的一种防倾杆的制备方法，其特征在于，所述浇铸过程中辅以机械振动，振动频率为...
【专利技术属性】
技术研发人员：华吉，华胜，
申请(专利权)人：宁波华源精特金属制品有限公司，
类型：发明
国别省市：浙江,33