The invention relates to a rGO/CNT three-dimensional composite conductive film for salt cutting. In the rGO/CNT three-dimensional composite conductive film, CNT interspersed in the rGO layer gap and forms a porous three-dimensional skeleton. The pure water flux is improved and the salt cutting rate of the rGO/CNT film is kept well. Compared with the existing conductive film with higher specific capacitance and conductivity, mechanical strength and stability, the invention skillfully integrates the retention effect of the membrane pore and the performance of the membrane as an electrode, so that the cutting salt rate of the applied voltage is significantly improved compared with that without the voltage.
【技术实现步骤摘要】
一种截盐用rGO/CNT三维复合导电膜及其制备方法和使用方法
本专利技术涉及水处理
，尤其涉及一种截盐用rGO/CNT三维复合导电膜及其制备方法和使用方法。
技术介绍
近年来，淡水短缺问题日益突出。发展低能耗和环境友好型的废水除盐和海水淡化技术是解决淡水危机的重要途径。目前常用的除盐技术有：反渗透、离子交换、蒸馏等，这些技术都存在成本高、能耗高等问题。相比之下，纳滤膜在常温低压下即可实现除盐，并且导电的纳滤膜通过外加电压可以进一步提高除盐的效率，其节能、无二次污染、操作简单的优势使得纳滤除盐脱颖而出。因此，大量研究者开始致力于探索具有多传输通道、高导电性和高机械强度的纳米膜材料，并将其应用于制备纳滤膜。现有技术中导电纳滤膜的材料大多采用高分子导电聚合物或碳纳米管。氧化石墨烯(GO)作为一种新型的二维纳米材料，由于其独特的片层结构、可调的物化特性、高导电性、化学和机械稳定性等优点已应用在膜材料上。但是由于含氧官能团的存在，GO层间距较大，水中盐离子可穿过，因此GO膜截盐效果不佳。为此，人们将GO膜进行还原，形成还原GO(rGO)，减小了GO层间距，有效提高了截...
【技术保护点】
一种截盐用rGO/CNT三维复合导电膜，其特征在于，所述rGO/CNT三维复合导电膜中，CNT穿插于rGO层间隙并相互交叉形成多孔三维骨架。
【技术特征摘要】
1.一种截盐用rGO/CNT三维复合导电膜，其特征在于，所述rGO/CNT三维复合导电膜中，CNT穿插于rGO层间隙并相互交叉形成多孔三维骨架。2.如权利要求1所述的截盐用rGO/CNT三维复合导电膜，其特征在于，所述截盐用rGO/CNT三维复合导电膜中CNT占比10～40wt％，优选15～33wt％。3.如权利要求1或2所述的截盐用rGO/CNT三维复合导电膜，其特征在于，所述截盐用rGO/CNT三维复合导电膜的截留分子量为100～800，优选200～300。4.如权利要求1～3任一项所述截盐用rGO/CNT三维复合导电膜的制备方法，其特征在于，所述制备方法包括如下步骤：(1)将GO和CNT按比例分散于水中得到混合水分散液；(2)以微孔膜为基底，将步骤(1)所得混合水分散液沉积在所述基底上，干燥后得到GO/CNT复合膜；(3)将步骤(2)所得GO/CNT复合膜还原得到截盐用rGO/CNT三维复合导电膜。5.如权利要求4所述的制备方法，其特征在于，步骤(1)所述混合水分散液中碳纳米管的浓度为1.5×10-3～6×10-3g/mL，优选2.25×10-3～4.95×10-3g/mL；优选地，所述...
【专利技术属性】
技术研发人员：胡承志，刘会娟，曲久辉，刘中桃，孙境求，
申请(专利权)人：中国科学院生态环境研究中心，
类型：发明
国别省市：北京,11