The invention discloses a preparation method of a polypropylene hollow fiber nanofiltration membrane. The invention uses melt spinning stretching method preparing polypropylene hollow fiber nanofiltration membrane, the nanofiltration membrane has the advantages of high strength, one layer support features functional layer; the preparation process, by controlling the spinning cooling bath composition, air gap length, stretching ratio and other factors can be functional layer suitable, by controlling the stretching ratio and stretching rate so as to control the size of pore size and porosity. The nanofiltration membrane has the advantages of simple preparation process and preparation process of no pollution, low cost, high strength film, the BSA rejection rate is 98 to 100%, sodium sulfate removal rate is 60 90%, under the pressure of 0.1MPa the flux is 5 50L/m
【技术实现步骤摘要】
聚丙烯中空纤维纳滤膜的制备方法
本专利技术涉及高分子材料
，尤其是一种聚丙烯中空纤维纳滤膜的制备方法。
技术介绍
纳滤膜孔径大小在1nm—10nm之间，按孔径大小分类介于超滤和反渗透之间的一种分离膜。20世纪70年代由J.E.Cadotte开始着手研究，80年代实现工业化。起初纳滤过程被称为“杂化过滤”，纳滤膜也被称为低压反渗透膜或疏松反渗透膜。后来由美国Film-Tech公司提出“纳滤”的概念，至今一直沿用。国内纳滤膜的研究则是从高从堦院士在全国膜学术交流会上介绍纳滤技术进展开始的。目前常用的纳滤膜材料有醋酸纤维素系列，芳香聚酰胺，磺化聚聚砜/醚砜等。常用的制备技术主要有相转化法、电荷化法、表面改性法、界面缩合法等等，除了相转化法是通过选材和调节铸模液配方以及铸膜工艺得到合适的膜以外，其他方法均是在基膜表面形成一层功能层。Ohya等采用溶剂蒸发法研制了用于石油炼制的芳香聚酰亚胺膜，溶剂蒸发时间为1min—3min，在癸二酸二辛酯中热处理成膜，该膜可截留分子量为170—400的小分子，其中部分制备的纳滤膜能有效的分离汽油和煤油【JournalofMembra...
【技术保护点】
一种聚丙烯中空纤维纳滤膜的制备方法，其特征在于，包括如下步骤：1)将聚丙烯原料通过挤出机加热挤出，再从喷丝头挤出，挤出物料经过长度为0.5‑3m气隙后进入冷却浴，最后再经卷绕设备牵伸得到聚丙烯初纺纤维；2)将聚丙烯初纺纤维在温度为110‑150℃的热环境中保温1h，得到硬弹性聚丙烯中空纤维；3)将硬弹性聚丙烯中空纤维进行拉伸，冷拉伸比例为5％‑20％之间，热拉伸比例为30‑95％，拉伸速率为10‑100mm/min，冷拉伸温度为20‑25℃，热拉伸温度为110‑140℃；拉伸之后在110‑140℃下热定型1h得到聚丙烯中空纤维纳滤膜。
【技术特征摘要】
1.一种聚丙烯中空纤维纳滤膜的制备方法，其特征在于，包括如下步骤：1)将聚丙烯原料通过挤出机加热挤出，再从喷丝头挤出，挤出物料经过长度为0.5-3m气隙后进入冷却浴，最后再经卷绕设备牵伸得到聚丙烯初纺纤维；2)将聚丙烯初纺纤维在温度为110-150℃的热环境中保温1h，得到硬弹性聚丙烯中空纤维；3)将硬弹性聚丙烯中空纤维进行拉伸，冷拉伸比例为5％-20％之间，热拉伸比例为30-95％，拉伸速...
【专利技术属性】
技术研发人员：韦福建，邵会菊，张凯舟，武晓，张敏敏，姚勇，靳进波，罗大军，
申请(专利权)人：贵州省材料产业技术研究院，
类型：发明
国别省市：贵州,52
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。