The invention discloses a modified nano SiO2 preparation method of fluorocarbon coatings, the key lies in the introduction of the modified nano SiO2 can increase the cross-linking polymerization of fluorocarbon resin and improve its ability in fluorocarbon coatings compatibility and dispersion properties, while the organic groups and fluorocarbon coatings modified nano SiO2 the surface of the co polymerization, formed with the cured film machine / inorganic hybrid network structure, nano SiO2 as rigid particles, the mechanical properties of fluorocarbon coatings play an enhanced role, can improve the self-cleaning and anti fouling ability of hydrophilic fluorocarbon resin coating, while improving the strength and corrosion resistance.
【技术实现步骤摘要】
用于氟碳涂料的改性纳米SiO2的制备方法引用基础本专利技术是原母案申请（申请号为：201510899715X）的分案申请。
本专利技术涉及一种用于氟碳涂料的改性纳米SiO２的制备方法。
技术介绍
氟碳涂料是指以氟树脂为主要成膜物质的涂料，氟树脂又称氟碳树脂，由于氟原子结构上的特点，将其引入到树脂中使得含氟树脂具有不同于其他树脂的特殊性能。在各种涂料之中，氟树脂涂料由于引入的氟元素电负性大，碳氟键能强，具有特别优越的各项性能。耐候性、耐热性、耐低温性、耐化学药品性，而且具有独特的不粘性和低摩擦性。经过几十年的快速发展，氟碳涂料在建筑、化学工业、电器电子工业、机械工业、航空航天产业、家庭用品的各个领域得到广泛应用。随着氟碳涂料的应用日益广泛，对其组分进行改进以期获得更加性能优越的涂层成为研究方向。众所周知，纳米材料与有机涂料相结合具有突出的特性，但纳米SiO2粒径小，比表面积大，亲水性能强，亲油性能差，在有机涂料中易团聚，难以均匀分散，限制了其优异性能的发挥。因此，对纳米SiO2改性以提高其和有机材料的相容性能，成为制备优异化工涂料的关键。纳米SiO2的改性主要有物理...
【技术保护点】
一种用于氟碳涂料的改性纳米SiO2的制备方法，包括如下步骤：在四口反应容器中将15重量份的纳米SiO2搅拌分散在200重量份的二甲苯中，缓慢依次加入30重量份的丙烯酸羟乙酯，0.5‑1重量份的对甲苯磺酸和0.2重量份的对苯二酚，升温至80‑90℃至回流，保温反应至无水生成后，继续反应3h，然后在真空环境中过滤，所得产物用甲苯洗涤3次以上，后用去离子水洗涤三次以上，置于50℃的鼓风干燥箱中干燥24小时得白色粉状固体。
【技术特征摘要】
1.一种用于氟碳涂料的改性纳米SiO2的制备方法，包括如下步骤：在四口反应容器中将15重量份的纳米SiO2搅拌分散在200重量份的二甲苯中，缓慢依次加入30重量份的丙烯酸羟乙酯，0.5-1重量份的对甲苯磺酸和0...