一种热反射型卷材涂料制造技术

本发明专利技术公开了一种热反射型卷材涂料，属于涂料技术领域，解决现有的预涂金属卷材涂料会吸收太阳能导致建筑物升温的技术问题，热反射型卷材涂料包括以下组份及各组分的重量比为：20～30份红外反射颜料、20～30份氟树脂、10～20份封闭异氰聚酸酯、1～3份助剂、35～50份稀释剂。本发明专利技术制备的热反射型卷材涂料以氟树脂作为主体树脂，红外反射颜料为功能颜料，红外反射颜料可反射大部分热量，从而改善建筑物因吸收太阳能导致的升温现象，使建筑物温度显著降低。

A kind of heat reflective coiling coating

The invention discloses a heat reflective coating, which belongs to the technical field to solve existing coatings, coil coatings can absorb solar energy technical problems lead to building heating, heat reflective coating comprises the following components and each component of the weight ratio of 20 to 30, 20 to 30 infrared reflective pigment samples 10 ~ 20 fluorine resin, closed isocyanate polyacid ester, 1 ~ 3, 35 ~ 50 diluent agent. Heat reflective coating prepared by the invention with fluorine resin as matrix resin, infrared reflective pigments as functional pigment, infrared reflecting pigments can reflect most of the heat, so as to improve the buildings because of the warming caused absorption of solar energy, the building temperature decreased significantly.

【技术实现步骤摘要】
一种热反射型卷材涂料
本专利技术属于涂料
，特别是涉及一种热反射型卷材涂料。
技术介绍
国内预涂金属卷材涂料的发展始于20世纪80年代中后期，由于其丰富的色彩、简单的生产工艺、优越的涂层性能，越来越多地被应用于建筑、汽车、家电面板等领域。预涂金属卷材具有良好的导热性，应用在建筑外墙及屋顶上时，更易吸收太阳能，使建筑物内温度上升，从而形成“城市热岛效应”。如何有效降低预涂金属卷材由于太阳光强烈辐射而引起的升温，使建筑物内降温节能成为了一个重要的研究课题。
技术实现思路
本专利技术所要解决的技术问题就是提供一种热反射型卷材涂料，解决现有的预涂金属卷材涂料会吸收太阳能导致建筑物升温的技术问题。为解决上述技术问题，本专利技术采用如下技术方案：一种热反射型卷材涂料，包括以下组份及各组分的重量比为：进一步的，所述红外反射颜料为氧化铁红、氧化铁黄和群青中的任意一种或任意两种构成的混合物。本专利技术的有益效果为：以氟树脂作为主体树脂，红外反射颜料为功能颜料，红外反射颜料可反射大部分热量，从而改善建筑物因吸收太阳能导致的升温现象，使建筑物温度显著降低，而氟树脂具有优异的耐候性，与封闭异氰聚酸酯可形成本文档来自技高网...

【技术保护点】
一种热反射型卷材涂料，其特征在于，包括以下组份及各组分的重量比为：

【技术特征摘要】
1.一种热反射型卷材涂料，其特征在于，包括以下组份及各组分的重量比为：2.根据权利要求1所述的一种热反...

【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：嘉兴御创电力科技有限公司，
类型：发明
国别省市：浙江,33