一种二茂铁修饰的铁基金属‑有机骨架材料类Fenton催化剂制备方法技术
Fe based metal organic framework materials Fenton prepared a two ferrocene modified preparation method
The invention discloses a ferrous metal organic framework materials Fenton prepared a two ferrocene modified preparation method. First of all, through the solvothermal synthesis of iron-based metal organic framework materials containing amino group (NH2 MIL (Fe)), then using the method after modified by NH2, MIL (Fe) carbonyl amino and two ferrocene formaldehyde condensation, two ferrocene fixed at NH2 MIL (Fe) on the preparation of MIL (Fe) Fc catalyst. The catalyst has high catalytic activity, environmental friendliness, easy recovery, and can be reused. It can efficiently degrade organic pollutants in water in a wide range of pH values. It has great application prospects.
【技术实现步骤摘要】
一种二茂铁修饰的铁基金属-有机骨架材料类Fenton催化剂制备方法
本专利技术属于废水处理领域，具体涉及一种二茂铁修饰的铁基金属-有机骨架材料类Fenton催化剂制备方法。
技术介绍
基于硫酸根自由基的高级氧化技术在近年得到快速发展，它以过硫酸盐（S2O82−）做氧化剂，通过多种方式催化分解生成高氧化性的硫酸根自由基（SO4−•），例如，紫外光、热、过渡金属等激活方式。在这些激活方式中，均一相铁盐或钴盐的催化活性受pH值影响大，不能回收利用，且存在潜在毒性。所以，异相催化剂如Fe3O4、Co3O4等成为研究的热点。其中Fe3O4是一种性能优良的异相类Fenton反应催化剂，能催化分解过硫酸盐产生硫酸自由基、羟基等，以降解废水中的生物难降解有机污染物，但是其催化效果并不能令人满意，存在催化活性低、氧化剂利用率低和有机物降解不彻底等问题。金属-有机骨架材料（metal-organicframeworks,MOFs）是由金属离子和有机配体通过自组装而成的具有多孔结构的晶体材料。与传统催化剂相比，MOFs具有不同的成分和结构，更高的比表面积和孔隙体积、大量的孔隙度，可调节...
【技术保护点】
一种二茂铁修饰的铁基金属‑有机骨架材料类Fenton催化剂制备方法，其特征在于：按以下步骤进行，（1）NH2‑MIL(Fe)的制备：将2‑氨基对苯二甲酸超声分散于N, N‑二甲基甲酰胺（DMF）中，用一定量NaOH溶液调节pH值，再加入FeCl3·6H2O或Fe(NO3)3·9H2O中的一种，使有机配体和Fe
【技术特征摘要】
1.一种二茂铁修饰的铁基金属-有机骨架材料类Fenton催化剂制备方法，其特征在于：按以下步骤进行，（1）NH2-MIL(Fe)的制备：将2-氨基对苯二甲酸超声分散于N,N-二甲基甲酰胺（DMF）中，用一定量NaOH溶液调节pH值，再加入FeCl3·6H2O或Fe(NO3)3·9H2O中的一种，使有机配体和Fe3+浓度分别为15.0～36.2g/L和9.3～11.2g/L，在室温下磁力搅拌15min，使其混合均匀，然后封装在具有聚四氟乙烯内衬的反应釜中，在100～160℃下反应5～24h，冷却至室温；离心分离，在25～60℃下用水、乙醇进行洗涤，最后在60℃下真空干燥24h即可，所制备的NH2-MIL(Fe)为NH2...
【专利技术属性】
技术研发人员：王钰，国伟林，郭怀苏，王瑞芹，韩凤，卫静，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。