一体式液压蓄能器胶囊的制作方法技术

一种液压蓄能器胶囊的制作方法，包括以下步骤:在充气的气囊上用胶片贴合成胶囊坯；将胶囊坯放入硫化装置内进行硫化形成胶囊初产品；将胶囊初产品中的充气气囊中气体放掉，取出气囊，并将硫化后的胶囊初产品自然冷却至室温形成胶囊成品。利用这种制作方法制作的胶囊，整体一次硫化成型，壁厚均匀，内外表面均光滑，疲劳寿命长，简化了工艺，产品质量高且稳定性好。

Preparation method of integrated hydraulic accumulator capsule

A method for production of hydraulic accumulator capsule, which comprises the following steps: sticking capsule blank film in the inflatable air bag; the capsule blank in a vulcanizing device in vulcanization forming capsule products at the beginning of the capsule; early inflatable balloon in air, in the product out of bag, and after the initial product curing capsule natural cooling to room temperature to form capsule products. The capsule made by this method is vulcanized and vulcanized at the same time, with uniform wall thickness, smooth inside and outside surface and long fatigue life. It simplifies the process, and has high quality and good stability.

【技术实现步骤摘要】
【国外来华专利技术】一体式液压蓄能器胶囊的制作方法
本专利技术涉及一种一体式液压蓄能器胶囊的制备方法,属于胶囊制备

技术介绍
蓄能器胶囊，是胶囊式蓄能器的重要组成部分，现有技术的蓄能器胶囊由橡胶制成，具有可伸缩性，用于储藏压缩后的惰性气体。胶囊内会注入一定气压的氮气，在胶囊外则是充入液压油，胶囊会随着液压油的挤压而变形，从而压缩氮气来蓄能，反之则是释放能量。如图1所示，蓄能器由耐压壳体、弹性胶囊、充气阀、提升阀、油口等组成，其关键部分是胶囊与壳体，胶囊尤其重要，胶囊是决定产品质量、寿命的关键因素。蓄能器胶囊的功能主要为：存储能量、吸收液压冲击、消除脉动和回收能量四大类。现有技术的橡胶胶囊充压前后的体积变化不足1倍，不能大量吸收脉动压力和流量中的能量，因此存储能量不足，热膨胀补偿性能差，不能吸收液压冲击，无法消除脉动、降噪。因此存在如下缺陷：1.体积变化量较小，无法有效吸收压力脉动;2.缓和冲击压力的功能不足;3.使用寿命短。造成上述缺陷的原因是：现有技术的蓄能器胶囊通过体积与外形与胶囊的内芯模具成型，导致成型集聚内应力；硫化后胶囊体积变化量小，无法有效吸收压力脉动；通过有内芯的模具成型后分体硫本文档来自技高网...

【技术保护点】
一种液压蓄能器胶囊的制作方法，其特征在于，包括:在充气的气囊上用胶片贴合成胶囊坯。

【技术特征摘要】
【国外来华专利技术】1.一种液压蓄能器胶囊的制作方法，其特征在于，包括:在充气的气囊上用胶片贴合成胶囊坯。2.根据权利要求1所述的液压蓄能器胶囊的制作方法，其特征在于，还包括：将胶囊坯放入硫化装置内进行...

【专利技术属性】
技术研发人员：赵慧江，赵腾宇，
申请(专利权)人：石家庄市西姆克科技有限责任公司，
类型：发明
国别省市：河北,13