The invention discloses a drum brake brake friction materials, including the weight of raw materials: steel wool: 8 ~ 15, 5 ~ 18: iron powder; foam iron powder: 5 ~ 18; NBR: 6 ~ 10; artificial graphite particles: 4 ~ 12; brass fiber from 2 to 8; copper fiber: 4 ~ 10; antimony: 3 ~ 5; 4 to 12 parts: vermiculite; collagen fiber: 2 ~ 5; alumina: 0.5 ~ 2; Magnesium Oxide: 3 ~ 6; petroleum coke: 10 ~ 20; ceramic fiber: 4 ~ 12; aramid pulp: 0.5 ~ 2; the preparation method of the invention also discloses a brake drum brake friction material, adopting the technical scheme of the invention overcomes the defects of the existing technology of high-speed vehicle brake friction energy when the brake failure caused the defect of safety accidents, avoid high-speed braking when Ann The whole accident occurred, and the service life of the brake shoe friction material was improved.
【技术实现步骤摘要】
一种鼓式制动器刹车蹄摩擦材料及其制备方法
本专利技术属于煤矿开采领域，更具体地说，本专利技术涉及一种鼓式制动器刹车蹄摩擦材料及其制备方法。
技术介绍
鼓式制动器刹车蹄摩擦材料，在汽车工业中属于关键的安全件，汽车的启动、制动和驻车都离不开摩擦材料，摩擦材料的好坏、优劣直接关系生命财产安全；摩擦材料是一类以摩擦为主要功能，兼有结构性能要求的复合材料，在工作时主要承受反复变化的机械应力场与热应力场，而力与热的发生源是无限形成新工作面的摩擦界面，摩擦材料在汽车工业中既是保安件，又是易损件，在汽车中用量不很大，但在汽车厢材中占有特殊重要的地位，随着石棉基摩擦材料的退出，新的材料被大量应用于现代汽车工业，汽车的轻型化和车速的不断提升，对启动、制动和驻车的灵敏度要求越来越高，尤其是汽车高速行驶制动摩擦动能大时，刹车温度高引起的刹车片摩擦块强度降低导致掉块、开裂等现象的发生，甚至汽车在高速制动时会导致安全事故的发生。
技术实现思路
本专利技术所要解决的技术问题是提供一种避免高速制动时安全事故发生的鼓式制动器刹车蹄摩擦材料。本专利技术还公开了一种鼓式制动器刹车蹄摩擦材料的制备的方法。为...
【技术保护点】
一种鼓式制动器刹车蹄摩擦材料，其特征在于：包括下述重量份的原料：钢棉：8～15份，还原铁粉：5～18份；泡沫铁粉：5～18份；丁晴橡胶：6～10份；人造颗粒石墨：4～12份；黄铜纤维：2～8份；紫铜纤维：4～10份；硫化锑：3～5份；膨胀蛭石：4～12份；胶原蛋白纤维：2～5份；氧化铝：0.5～2份；氧化镁：3～6份；石油焦：10～20份；陶瓷纤维：4～12份；芳纶浆粕：0.5～2份。
【技术特征摘要】
1.一种鼓式制动器刹车蹄摩擦材料，其特征在于：包括下述重量份的原料：钢棉：8～15份，还原铁粉：5～18份；泡沫铁粉：5～18份；丁晴橡胶：6～10份；人造颗粒石墨：4～12份；黄铜纤维：2～8份；紫铜纤维：4～10份；硫化锑：3～5份；膨胀蛭石：4～12份；胶原蛋白纤维：2～5份；氧化铝：0.5～2份；氧化镁：3～6份；石油焦：10～20份；陶瓷纤维：4～12份；芳纶浆粕：0.5～2份。2.按照权利要求1所述的一种鼓式制动器刹车蹄摩擦材料，其特征在于：所述的原料为粉末状，颗粒度<100目。3.一种按照权利要求1～2所述的鼓式制动器刹车蹄摩擦材料的制备方法，其特征在于：包括下述步骤：1)...
【专利技术属性】
技术研发人员：木文豹，木晓航，潘暖，
申请(专利权)人：安徽博耐克摩擦材料有限公司，
类型：发明
国别省市：安徽,34