The invention discloses a lightweight plastic and its manufacturing method. The lightweight plastic includes the following weight parts: 50~90 red sand, 2~20 fireclay, 2~20 bentonite, 1~30 waste paper and 0.01 to 0.5 parts of clay dispersing agent. The lightweight plastic of the invention is suitable for masonry of industrial high-temperature kiln walls and furnace roof, and heat insulation of casting ingot head, and has the advantages of high temperature, high intensity, wide application scope and low cost. The light of the invention can be used for plastics and plastic products containing fibrous pores, with insulation and ventilation, long time use temperature is 1300 degrees centigrade, short time use temperature is 1550 degrees centigrade, its broad source of raw materials, low price, simple production process and easy to popularize.
【技术实现步骤摘要】
一种轻质可塑料及其制作方法
本专利技术属于耐火材料
，具体涉及一种轻质可塑料及其制作方法。
技术介绍
高温工业窑炉为减少散热、提高热效率，通常在炉墙及炉顶采用轻质可塑料砌筑，尤其是炉顶采用轻质耐火材料可大幅度减轻炉顶重量。常见材料有：硅酸铝纤维板、纤维毡，其最高使用温度(1100℃)低、强度低，使用范围受到限制，轻质粘土砖、高铝砖等定型制品适用于大面积的墙体砌筑，其在形状复杂的部位及窑炉非拱形炉顶部位不适用，并且上述材料的成本相对较高。浇铸大型钢锭时，钢锭帽口需要轻质耐火材料对钢锭头部进行保温，以减少钢锭凝固过程中产生缩孔疏松缺陷。因此，有必要开发一种用于各种高温工业窑炉、铸造行业的轻质可塑料及其制作方法、施工方法及制品。
技术实现思路
本专利技术的第一目的在于提供一种用于各种高温工业窑炉、铸造行业的轻质可塑料，第二目的在于提供所述的轻质可塑料的制作方法，第三目的在于提供所述的轻质可塑料的施工方法，第四目的在于提供所述的轻质可塑料的制品。本专利技术的第一目的是这样实现的，所述的轻质可塑料包括以下重量份的原料：红砂50～90份，耐火粘土2～20份，膨润土2～20份...
【技术保护点】
一种轻质可塑料，其特征在于所述的轻质可塑料包括以下重量份的原料：红砂50～90份，耐火粘土2～20份，膨润土2～20份，废纸纤维1～30份，粘土分散剂0.01～0.5份。
【技术特征摘要】
1.一种轻质可塑料，其特征在于所述的轻质可塑料包括以下重量份的原料：红砂50～90份，耐火粘土2～20份，膨润土2～20份，废纸纤维1～30份，粘土分散剂0.01～0.5份。2.根据权利要求1所述的轻质可塑料，其特征在于所述的轻质可塑料包括以下重量份的原料：红砂75～87份，耐火粘土4～10份，膨润土4～10份，废纸纤维5～15份，粘土分散剂0.05～0.1份。3.根据权利要求1或2所述的轻质可塑料，其特征在于所述的红砂的SiO2含量88％以上，粒度为0～1mm。4.根据权利要求1或2所述的轻质可塑料，其特征在于所述的耐火粘土为软质耐火粘土细粉，所述的细粉粒度为180～200目。5.根据权利要求1或2所述的轻质可塑料，其特征在于所述的膨润土为膨润土细粉，所述的细粉粒度为180～200目。6.根据权利要求1或2所述的轻质可塑料，其特征在于所述的废纸纤维为废报纸纤维。7.一种根据权利要求1～6任一所述的轻质可塑料的...
【专利技术属性】
技术研发人员：黄波，郑杰，崔娟，鲁志燕，
申请(专利权)人：云南濮耐昆钢高温材料有限公司，
类型：发明
国别省市：云南,53