The invention relates to a high temperature binder, weight percentage of its components are: bentonite 5% ~ 8%, 38% ~ 42%, silicon sol solution fluorine polymer silicate 20% ~ 25%, 6 ~ 10% alumina powder and water from 20% to 25%; and 100% components; method of preparation of high temperature binder using the above the first group: according to the required ratio of the components are prepared; then, bentonite, silica sol solution, poly silicate ester, corundum powder and water mixing, heating to 60 to 70 DEG C under the condition of standing 4 hours, and then cooled to 30 to 35 DEG C for 3 hours. Both high temperature adhesive. The invention has the advantages of better impact resistance and lower brittleness, and has the advantages of high temperature resistance and good adhesive strength of the inorganic binder, so as to improve the physical performance of the inorganic binder and better meet the actual production needs.
【技术实现步骤摘要】
一种高温粘结剂
本专利技术属于化工领域，特别涉及一种高温粘结剂。
技术介绍
高温粘结剂又叫高温粘合剂、高温结合剂、高温胶粘剂。为无色透明或略带黄色的粘稠液体，易溶于水，呈弱酸性，不含钠离子。适用于300℃以上高温条件下粘结，尤其适用于高温炉窑砌筑或修补。如陶瓷等的粘接，各种高温炉窑、热处理炉砌筑和修补，炉窑轮修的喷补料，及粘贴硅酸铝耐火纤维等。其最高可耐温度1500℃，短时间可耐1800℃甚至更高。尤其在高温炉窑砌筑或修补上，与耐火材料调成的胶泥所砌筑的炉窑具有抗震、抗剥落、耐骤冷骤热、耐高温气流冲刷、砖与砖结合牢固、不掉砖、不跑火等特点。由于不含钠离子，在粘贴硅酸铝耐火纤维时，可防止产生莫来石粉状结晶，且施工养护方便，可节能30%～50%；用于砌筑炉窑或修补炉窑，可延长窑炉寿命1～3倍，减少了工厂修炉费用和停工损失。但是目前使用的高温粘结剂成本较高，不能很好的适应市场的需要。
技术实现思路
本专利技术的目的是提供一种成本低廉且粘接效果良好的高温粘结剂。一种高温粘结剂，其组分的重量百分比为：膨润土5%～8%、硅溶胶溶液38%～42%、氟聚硅酸酯20%～25%、刚玉粉6...
【技术保护点】
一种高温粘结剂，其特征在于：所述高温粘结剂组分的重量百分比为：膨润土5%～8%、硅溶胶溶液38%～42%、氟聚硅酸酯20%～25%、刚玉粉6～10%、水20%～25%；各组分之和为100%；采用上述组分制备高温粘结剂的制备步骤为：先按所需用量比例将各组分备好；然后将膨润土、硅溶胶溶液、氟聚硅酸酯、刚玉粉与水混合搅拌均匀，加热至60～70℃的条件下静置4小时，然后降温至30～35℃熟化3小时，既得高温粘结剂。
【技术特征摘要】
1.一种高温粘结剂，其特征在于：所述高温粘结剂组分的重量百分比为：膨润土5%～8%、硅溶胶溶液38%～42%、氟聚硅酸酯20%～25%、刚玉粉6～10%、水20%～25%；各组分之和为100%；采用上述组分制备高温粘结剂的制备步骤为：先按所需用量比例将各组分备好；然后将膨润土、硅...
【专利技术属性】
技术研发人员：程海霞，
申请(专利权)人：如皋市康利化工有限公司，
类型：发明
国别省市：江苏,32