The invention provides a modified chloroprene rubber and its preparation method, the modified chloroprene rubber is prepared from the following components by weight: 90 to 100 portions of chloroprene rubber, natural rubber 60 ~ 80 ~ 3, Magnesium Oxide 6, Zinc Oxide 0.5 ~ 1.5, 3 ~ 5 accelerator from 1 to 3, vulcanizing agent, stearic acid, 0.5 to 1.5 portions of antiscorcher CTP 1 ~ 3, 3 ~ 8 phr carbon black adhesive, 15 ~ 25, 3 ~ 6 o two butyl and 12 II polyester 12 ~ 16 qi. The present invention adopts the combination of natural rubber and chloroprene rubber, effectively improves the hardness and cold resistance of the traditional chloroprene rubber, and has high use strength, and the modified chloroprene rubber is more suitable for the rubber pad, cushion and solid tire products with higher rubber hardness.
【技术实现步骤摘要】
一种改性氯丁橡胶及其制备方法
本专利技术涉及合成橡胶
，尤其涉及一种高硬度、高耐寒性的改性氯丁橡胶及其制备方法。
技术介绍
氯丁橡胶，又名氯丁二烯橡胶，具有良好的物理机械性能，耐油，耐热，耐燃，耐日光，耐臭氧，耐酸碱，耐化学试剂；具有较高的拉伸强度、伸长率和可逆的结晶性，粘接性好。耐油、耐化学腐蚀性优异。耐油性仅次于丁腈橡胶，耐候性和耐臭氧老化仅次于乙丙橡胶和丁基橡胶，耐热性与丁腈橡胶相当，具有一定的阻燃性。基于氯丁橡胶优异的特性，被广泛应用于各种领域，其中制鞋及建筑领域用胶黏剂是我国氯丁橡胶最大的应用领域，约占总消费量的60％；其次是工业橡胶制品，约占总消费量的30％；另外有约10％用于电线电缆及其他领域。目前，传统的氯丁橡胶存在着耐寒性稍差、硬度低、贮存稳定性较差等问题，且工业需求大，国内供不应求，依赖进口，生产过程存在着原材料、公用工程消耗高，副产品多、产品品种少、质量差且不稳定，排放污水、废气多，生产安全性较差等缺陷。特别是，基于现有氯丁橡胶存在的硬度低、拉伸强度弱的弊端，在橡胶部件中与金属件间的结合力不够，大大影响其在橡胶硬度较大的橡胶垫块、软垫及...
【技术保护点】
一种改性氯丁橡胶，其特征在于，所述改性氯丁橡胶由以下重量份的组分制成：氯丁橡胶90～100份，天然橡胶60～80份，氧化镁3～6份，氧化锌0.5～1.5份，促进剂3～5份，硫化剂1～3份，硬脂酸0.5～1.5份，防焦剂CTP 1～3份，粘合剂3～8份，炭黑15～25份，邻二丁酯3～6份和12‑Ⅱ齐聚酯12～16份。
【技术特征摘要】
1.一种改性氯丁橡胶，其特征在于，所述改性氯丁橡胶由以下重量份的组分制成：氯丁橡胶90～100份，天然橡胶60～80份，氧化镁3～6份，氧化锌0.5～1.5份，促进剂3～5份，硫化剂1～3份，硬脂酸0.5～1.5份，防焦剂CTP1～3份，粘合剂3～8份，炭黑15～25份，邻二丁酯3～6份和12-Ⅱ齐聚酯12～16份。2.根据权利要求1所述的一种改性氯丁橡胶，其特征在于，所述天然橡胶为烟片胶。3.根据权利要求1或2所述的一种改性氯丁橡胶，其特征在于，所述促进剂为促进剂DM和/或促进剂TMTD。4.根据权利要求1或2所述的一种改性氯丁橡胶，其特征在于，所述硫化剂为硫磺，有机多硫化物、过氧化物、金属氧化物中的一种或多种。5.根据权利要求1所述的一种改性氯丁橡胶，其特...
【专利技术属性】
技术研发人员：闻浩泉，陈国良，倪志文，王平，杨建，邱国华，
申请(专利权)人：浙江久运汽车零部件有限公司，
类型：发明
国别省市：浙江,33