一种羽毛球球头材料制造技术

本发明专利技术公开了一种羽毛球球头材料，它是由以下重量份的原料组成：氯丁橡胶100重量份、氯醇橡胶30重量份、二丁基酞酸酯5重量份、纳米氧化锌2重量份、硬脂酸1‑3重量份、亚克力粉2‑4重量份、磷酸铝1‑3重量份、石蜡1‑5重量份、四氟乙烯6‑8重量份、三元乙丙橡胶8‑10重量份。本发明专利技术专门针对羽毛球球头提供的材料，组分配置合理，成本低，制作的球头抗击打能力强，抗老化，耐酸碱，耐高温等，深受消费者喜欢。

A badminton ball head material

The invention discloses a badminton ball material, which is composed of the following raw materials in weight portion: 100 portions of chloroprene rubber, epichlorohydrin rubber, butyl phthalate 30 weight two 5 weight portions, nano Zinc Oxide 2 weight portions, stearic acid 1 3 weight portions, acrylic powder in 4 weight portions, 2 1 to 3 parts by weight of aluminum phosphate, paraffin 1 5 weight portions, 6 tetrafluoroethylene in 8 weight portions, three yuan 8 10 weight portions of ethylene propylene rubber. The invention specially aims at the material provided by the badminton ball head, the components are reasonable in configuration, low in cost, strong in fighting ability, anti-aging, acid and alkali resistant, high temperature resistant, etc., and is well liked by consumers.

【技术实现步骤摘要】
一种羽毛球球头材料
本专利技术涉及体育用品
，尤其涉及一种羽毛球球头材料。
技术介绍
羽毛球是一项室内、室外兼顾的运动。依据参与的人数，可以分为单打与双打，及新兴的3V3规则。羽毛球在使用过程中，羽毛球球头会粘附一些油污、灰尘等，严重影响羽毛球的使用效果。本专利技术提出一种羽毛球球头材料。
技术实现思路
为克服上述不足，本专利技术提供一种羽毛球球头材料。本专利技术是采取以下技术方案来实现的：一种羽毛球球头材料，它是由以下重量份的原料组成：氯丁橡胶100重量份、氯醇橡胶30重量份、二丁基酞酸酯5重量份、纳米氧化锌2重量份、硬脂酸1-3重量份、亚克力粉2-4重量份、磷酸铝1-3重量份、石蜡1-5重量份、四氟乙烯6-8重量份、三元乙丙橡胶8-10重量份。进一步地，它是由以下的原料组成：氯丁橡胶100重量份、氯醇橡胶30重量份、二丁基酞酸酯5重量份、纳米氧化锌2重量份、硬脂酸2重量份、亚克力粉3重量份、磷酸铝2重量份、石蜡3重量份、四氟乙烯7重量份、三元乙丙橡胶9重量份。综上所述本专利技术具有以下有益效果：本专利技术专门针对羽毛球球头提供的材料，组分配置合理，成本低，制作的球头抗击打能力强本文档来自技高网...

【技术保护点】
一种羽毛球球头材料，其特征在于：它是由以下重量份的原料组成：氯丁橡胶100重量份、氯醇橡胶30重量份、二丁基酞酸酯5重量份、纳米氧化锌2重量份、硬脂酸1‑3重量份、亚克力粉2‑4重量份、磷酸铝1‑3重量份、石蜡1‑5重量份、四氟乙烯6‑8重量份、三元乙丙橡胶8‑10重量份。

【技术特征摘要】
1.一种羽毛球球头材料，其特征在于：它是由以下重量份的原料组成：氯丁橡胶100重量份、氯醇橡胶30重量份、二丁基酞酸酯5重量份、纳米氧化锌2重量份、硬脂酸1-3重量份、亚克力粉2-4重量份、磷酸铝1-3重量份、石蜡1-5重量份、四氟乙烯6-8重量份、三元乙丙橡胶8-10重...