The invention discloses a cable sheath material wear resistance and tensile, the raw materials according to parts by weight: 40 chloroprene rubber styrene butadiene rubber 10 60 copies, 20 copies, 35 copies of 25 polypropylene, crosslinking agent, modified lauric acid 10 15 copies, 35 copies of calcined kaolin 25, 15 cotton fiber 25 copies, 10 copies of the 5 medical stone powder, heavy calcium carbonate, 20 30 copies, 4 copies of 2 disproportionated rosin, three phosphoric acid phenyl ester 1.5 stearic acid 2 2.5 copies, 4 copies, 3 copies of antioxidant 2. The crosslinking agent by weight: two cumene peroxide 2 4 copies, 2 copies of 1 sulfur. The wear resistant and tensile cable sheath material proposed by the invention has excellent tensile strength and wear resistance effect, and has low cost.
【技术实现步骤摘要】
一种耐磨耐拉伸的电缆护套材料
本专利技术涉及电缆护套
，尤其涉及一种耐磨耐拉伸的电缆护套材料。
技术介绍
目前，随着社会经济的发展，电线电缆用量迅速增长，对电缆的质量要求也不断的提高，现有的电缆在加工过程中因其选料不合理，导致电缆抗拉强度和耐磨损性能并不能满足人们的需求，给人们后期的使用带来很大的问题。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种耐磨耐拉伸的电缆护套材料，抗拉强度和耐磨损效果极好，而且成本低廉。本专利技术提出的一种耐磨耐拉伸的电缆护套材料，其原料按重量份包括：氯丁橡胶40-60份，丁苯橡胶10-20份，聚丙烯25-35份，交联剂3-6份，改性月桂酸10-15份，煅烧高岭土25-35份，棉纤维15-25份，麦饭石粉5-10份，重质碳酸钙20-30份，歧化松香2-4份，磷酸三苯酯1.5-2.5份，硬脂酸2-4份，防老剂2-3份。优选地，交联剂按重量份包括：过氧化二异丙苯2-4份，硫磺1-2份。优选地，改性月桂酸采用如下工艺制备：将聚乙烯醇、三乙烯四胺、N,N'-二琥珀酰亚胺基碳酸酯、乙腈混合，调节温度搅拌，升温，加入月桂酸、淀粉、...
【技术保护点】
一种耐磨耐拉伸的电缆护套材料，其特征在于，其原料按重量份包括：氯丁橡胶40‑60份，丁苯橡胶10‑20份，聚丙烯25‑35份，交联剂3‑6份，改性月桂酸10‑15份，煅烧高岭土25‑35份，棉纤维15‑25份，麦饭石粉5‑10份，重质碳酸钙20‑30份，歧化松香2‑4份，磷酸三苯酯1.5‑2.5份，硬脂酸2‑4份，防老剂2‑3份。
【技术特征摘要】
1.一种耐磨耐拉伸的电缆护套材料，其特征在于，其原料按重量份包括：氯丁橡胶40-60份，丁苯橡胶10-20份，聚丙烯25-35份，交联剂3-6份，改性月桂酸10-15份，煅烧高岭土25-35份，棉纤维15-25份，麦饭石粉5-10份，重质碳酸钙20-30份，歧化松香2-4份，磷酸三苯酯1.5-2.5份，硬脂酸2-4份，防老剂2-3份。2.根据权利要求1所述耐磨耐拉伸的电缆护套材料，其特征在于，交联剂按重量份包括：过氧化二异丙苯2-4份，硫磺1-2份。3.根据权利要求1或2所述耐磨耐拉伸的电缆护套材料，其特征在于，改性月桂酸采用如下工艺制备：将聚乙烯醇、三乙烯四胺、N,N'-二琥珀酰亚胺基碳酸酯、乙腈混合，调节温度搅拌，升温，加入月桂酸、淀粉、脂肪酶搅拌，加入无水乙醇沉淀，过滤，喷雾干燥得到改性月桂酸。4.根据权利要求1-3任一...
【专利技术属性】
技术研发人员：赵家玉，
申请(专利权)人：铜陵市铜都特种线缆有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。