With micro expansion superfine composite modified limestone for concrete, which comprises the following parts by weight of raw materials, 75 90 clastic limestone, wollastonite is 3 6, such as fly ash for 10 20, 20 to 10 lithium slag; excitation of modified materials doped outside adding, the modified excitation weight the percentage of materials for Ultrafine Composite modified limestone for desulfurization gypsum as the total, 2% 4%, triethanolamine was 0.03% 0.05%, maltodextrin 0.05% 0.15%, sulphoaluminate cement is 2% 6%. The invention adds functional modified activated materials by ultrafine grinding and chemical excitation double modification in the limestone clasts, such as fly ash, silica fume, lithium slag, not only conducive to the early and late activity increased, at the same time it has expansion function, enhance the crack resistance of concrete; improve the fluidity of the powder superfine composite modified limestone powder, which makes it easy to transport gas, and is not easy to agglomerate empty arch.
【技术实现步骤摘要】
一种混凝土用微膨胀超细复合改性石灰石粉
本专利技术涉及混凝土领域，确切地说是一种混凝土用微膨胀超细复合改性石灰石粉。
技术介绍
我国目前正处于基础设施建设高峰期，建设规模巨大，建筑结构以钢筋混凝土结构形式为主体。据统计我国商品混凝土近年来的趋势是基本保持年产量在24亿吨左右，占世界的一半以上，虽然水泥混凝土行业完全处于供给结构性过剩的状态，但矿物掺合料并没有产能过剩。由于国内钢铁工业也严重产能过剩，粉煤灰、矿渣等工业废渣资源的分布不均匀，产量正在逐年降低，矿渣、粉煤灰等高活性混合材产出量实际上在逐年减少，国内许多地区常规的混凝土矿物掺和料已是极其短缺的原料。石灰石粉是以生产石灰石碎石和机制砂石产生的细砂和石屑为原料,通过进一步粉磨工艺得到的细粉,因为在混凝土中具有良好的减水和填充效应而被关注和应用。近年来的研究，证实石灰石粉可作为混凝土矿物掺和料的组成部分应用于混凝土中，可以补充粉煤灰供应的不足,但在目前实际工程应用中，还存在石灰石微粉气体输送效果差、存储于混凝土搅拌站筒罐中易空拱结块以及活性指数值低、掺入混凝土中混凝土易出现泌水、收缩开裂的问题。
技术实现思路
本专...
【技术保护点】
一种混凝土用微膨胀超细复合改性石灰石粉，包括以下重量份的原料，石灰石碎屑为75‑90，硅灰为3‑6，等外粉煤灰为10‑20，锂渣为10‑20；激发改性材料以外掺的方式掺入，各改性激发材料占上述超细复合改性石灰石粉总量的重量百分比为，脱硫石膏为2%‑4%，三乙醇胺为0.03%‑0.05%，麦芽糊精为0.05%‑0.15%，硫铝酸盐水泥为2%‑6%。
【技术特征摘要】
1.一种混凝土用微膨胀超细复合改性石灰石粉，包括以下重量份的原料，石灰石碎屑为75-90，硅灰为3-6，等外粉煤灰为10-20，锂渣为10-20；激发改性材料以外掺的方式掺入，各改性激发材料占上述超细复合改性石灰石粉总量的重量百分比为，脱硫石膏为2%-4%，三乙醇胺为0.03%-0.05%，麦芽...