二氧化硅纳米颗粒表面修饰氨基的方法技术
Method for surface modification of amino groups on silica nanoparticles
Methods silica nanoparticles surface modified with amino, toluene as dispersant, preparation of silica nanoparticles suspension, the toluene and silica are anhydrous; adding 3 aminopropyltrimethoxysilane to silica nanoparticles in solution, stirring to the mixing; heating and refluxing in the heating process of continuous nitrogen into protection the recovered samples, using anhydrous ethanol; centrifugal washing, storage and dispersed in ethanol, silica nanoparticles surface modified amino. The invention can be successfully modified in the SiO2 more NPs amino, and the modified SiO2 NPs has good dispersibility and stability. At the same time, the strict anhydrous environment and inert atmosphere in the preparation process prevent the coupling agent from modifying the common hydrolysis products of SiO2, which makes the experiment process more operable and repeatable.
【技术实现步骤摘要】
二氧化硅纳米颗粒表面修饰氨基的方法
本专利技术属于二氧化硅纳米颗粒修饰领域，具体涉及一种利用3-氨基丙基三甲氧基硅烷（APTMS）在二氧化硅纳米颗粒表面偶联上含氨基的方法。
技术介绍
二氧化硅（SiO2）是一种常用的无机材料，具有优良的热稳定性和化学稳定性。纳米二氧化硅因其具有的小尺寸效应、表面界面效应、量子尺寸效应以及高温下仍具有的高强、高韧、稳定性好等特性，更是广泛应用于塑料、橡胶、陶瓷、涂料、化妆品、药物载体等材料的制备改性上。但由于二氧化硅纳米颗粒（SiO2NPs）表面含有大量羟基（-OH），使其表面能较高，亲水性强，易团聚，与有机基体的相容性和分散性差，必须对SiO2NPs表面进行有机修饰，以降低表面能、提高分散性，方可将SiO2的优异特性赋予复合材料。硅烷偶联剂是诸多SiO2表面修饰剂中最常用的一种，SiO2NPs经过氨基硅烷偶联剂修饰的表面含有氨基（-NH2），活性氨基可以和很多分子发生反应，并可以显著提高SiO2NPs的分散性和稳定性，从而拓展和提高SiO2的应用性能。如在材料领域，修饰后的SiO2NPs作为补强填料添加到橡胶、塑料等材料中，能有效...
【技术保护点】
二氧化硅纳米颗粒表面修饰氨基的方法，其特征在于步骤为：a. 以甲苯作为分散剂，配制5mM~8.5mM粒径为200nm的二氧化硅纳米颗粒浊液，其中甲苯及二氧化硅中均无水；b. 向二氧化硅纳米颗粒浊液中加入不低于0.5vol.%的氨基硅烷偶联剂，充分搅拌使其混匀；c. 控制温度85℃~105℃加热回流12h~15h，加热过程中持续通入氮气进行保护；d. 回收样品，使用无水乙醇离心洗涤，并分散在无水乙醇中储存，得表面修饰氨基的二氧化硅纳米颗粒。
【技术特征摘要】
1.二氧化硅纳米颗粒表面修饰氨基的方法，其特征在于步骤为：a.以甲苯作为分散剂，配制5mM~8.5mM粒径为200nm的二氧化硅纳米颗粒浊液，其中甲苯及二氧化硅中均无水；b.向二氧化硅纳米颗粒浊液中加入不低于0.5vol.%的氨基硅烷偶联剂，充分搅拌使其混匀；c.控制温度85℃~105℃加热回流12h~15h，加热过程中持续通入氮气进行保护；d.回收样品，使用无水...
【专利技术属性】
技术研发人员：王婷，丁锐，屈冠雯，王楚，
申请(专利权)人：东南大学，
类型：发明
国别省市：江苏,32